- Techmer ES Electrafil® J-3/CF/30 Nylon 6, 30% Carbon Fiber Reinforced
Techmer ES Electrafil® J-3/CF/30 Nylon 6, 30% Carbon Fiber Reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Carbon Fiber Filled |
| Manufacturer | Techmer ES |
| Trade Name | Electrafil® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES Electrafil® J-3/CF/30 Nylon 6, 30% Carbon Fiber Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.28 g/cc | 0.0462 lb/in³ | ASTM D792 |
| Water Absorption | 1.0 % | 1.0 % | 24 hrs. ASTM D570 |
| Linear Mold Shrinkage | 0.0010 cm/cm @Thickness 3.17 mm |
0.0010 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 228 MPa | 33000 psi | ASTM D638 |
| Elongation at Break | 3.3 % | 3.3 % | ASTM D638 |
| Tensile Modulus | 19.3 GPa | 2800 ksi | ASTM D638 |
| Flexural Yield Strength | 317 MPa | 46000 psi | ASTM D790 |
| Flexural Modulus | 17.2 GPa | 2500 ksi | ASTM D790 |
| Izod Impact, Notched | 0.961 J/cm @Thickness 3.17 mm |
1.80 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Izod Impact, Unnotched | 8.01 J/cm @Thickness 3.17 mm |
15.0 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 213 °C | 415 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0625 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00 - 10.0 ohm-cm | 1.00 - 10.0 ohm-cm | ASTM C611 |
| Surface Resistance | 100 - 1000 ohm | 100 - 1000 ohm | ASTM D4496 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics GELOY HRA222F ASA+PC (Asia Pacific)
- Resinlab® CYNERGY CA6007 Adhesive
- Sylvin Technologies 9980-90 Natural PVC Molding Compound
- SABIC Innovative Plastics ULTEM 2300R PEI
- A. Schulman CP851 High Flow, Injection Molding Grade
- ExxonMobil LDPE LD 100.BW Low Density Polyethylene Resin
- ExxonMobil Febis K Series 46
- BIW ASTM Class 2D4 Silicone Foam
Copyright © lookpolymers.com All Rights Reserved