Techmer ES ElastoblendÂ® PA6/6 IM L W Nylon 66

Category	Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Impact Grade
Manufacturer	Techmer ES
Trade Name	Elastoblend®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Techmer ES ElastoblendÂ® PA6/6 IM L W Nylon 66.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Availability: North AmericaForms: PelletsAdditive: Lubricant and Impact ModifierFeatures: Lubricant and Impact ModifiedProcessing Method: Injection MoldingInformation provided by TP Composites, Inc.

Physical Properties	Metric	English	Comments
Density	1.08 g/cc	0.0390 lb/inÂ³	ASTM D792
Water Absorption	1.3 % @Time 86400 sec	1.3 % @Time 24.0 hour	ASTM D570
Linear Mold Shrinkage, Flow	0.016 cm/cm @Thickness 3.17 mm	0.016 in/in @Thickness 0.125 in	ASTM D955

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	110	110	ASTM D785
Tensile Strength	52.4 MPa	7600 psi	ASTM D638
Elongation at Yield	48 %	48 %	ASTM D638
Flexural Yield Strength	79.3 MPa	11500 psi	ASTM D790
Flexural Modulus	1.72 GPa	250 ksi	ASTM D790
Izod Impact, Notched	1.82 J/cm @Thickness 3.17 mm, Temperature -40.0 Â°C	3.40 ft-lb/in @Thickness 0.125 in, Temperature -40.0 Â°F	ASTM D256
	8.54 J/cm @Thickness 3.17 mm, Temperature 22.8 Â°C	16.0 ft-lb/in @Thickness 0.125 in, Temperature 73.0 Â°F	ASTM D256
Izod Impact, Unnotched	NB @Thickness 3.17 mm	NB @Thickness 0.125 in	ASTM D256

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	79.2 Âµm/m-Â°C	44.0 Âµin/in-Â°F	ASTM D696
Deflection Temperature at 0.46 MPa (66 psi)	216 Â°C	420 Â°F	Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	71.1 Â°C	160 Â°F	Unannealed; ASTM D648

Electrical Properties	Metric	English	Comments
Volume Resistivity	2.00e+14 ohm-cm	2.00e+14 ohm-cm	ASTM D257
Dielectric Strength	17.3 kV/mm	440 kV/in	Method A (Short-Time); ASTM D149