- Techmer ES Elastoblend® PA6/6 GF14 IM HS L BK 14% Glass Filled
Techmer ES Elastoblend® PA6/6 GF14 IM HS L BK 14% Glass Filled
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 10% Glass Fiber Filled , Nylon 66, Glass Reinforced, Impact Grade , Nylon 66, Heat Stabilized |
| Manufacturer | Techmer ES |
| Trade Name | Elastoblend® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES Elastoblend® PA6/6 GF14 IM HS L BK 14% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 14% Filler by WeightAdditive: Heat Stabilizer, Lubricant and Impact ModifierFeatures: Heat Stabilized, Lubricant and Impact ModifiedUL File Number: E157318Appearance: BlackInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | ASTM D792 |
| Water Absorption | 0.90 % @Time 86400 sec |
0.90 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0016 cm/cm @Thickness 3.17 mm |
0.0016 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 111 | 111 | ASTM D785 |
| Tensile Strength, Yield | 91.0 MPa | 13200 psi | ASTM D638 |
| Elongation at Break | 6.0 % | 6.0 % | ASTM D638 |
| Flexural Strength | 117 MPa | 17000 psi | ASTM D790 |
| Flexural Modulus | 4.31 GPa | 625 ksi | ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm @Thickness 3.17 mm, Temperature -40.0 °C |
2.00 ft-lb/in @Thickness 0.125 in, Temperature -40.0 °F |
ASTM D256 |
| 1.60 J/cm @Thickness 3.17 mm, Temperature 22.8 °C |
3.00 ft-lb/in @Thickness 0.125 in, Temperature 73.0 °F |
ASTM D256 | |
| Izod Impact, Unnotched | NB @Thickness 3.17 mm |
NB @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 79.2 µm/m-°C | 44.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 252 °C | 485 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | Unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | ASTM D257 |
| Dielectric Strength | 19.3 kV/mm | 490 kV/in | Method A (Short-Time); ASTM D149 |
Users viewing this material also viewed the following:
- Nyco M325 WOLLASTOCOAT® Wollastonite
- SABIC Innovative Plastics Lexan® FXD123R PC (Europe-Africa-Middle East)
- Solvay Specialty Polymers Kalix® 2955 Polyamide, High Performance (HPPA), Glass Fiber
- SABIC Innovative Plastics LNP THERMOCOMP RF009H PA 66
- Cosmic Plastics 306 Orlon Filled Ortho Diallyl Phthalate Molding Compound
- Unipetrol PP MONSTEN® MT 230 Polypropylene Homopolymer
- Polyram RamTough PZ300G8 Polycarbonate, 40% Glass Fiber
- Eagle Brass 430 Ferritic Stainless Steel, Full Hardened
- Dow Corning LSPOG50 SILICONE MASTERBATCH ORANGE
- DuPont Teijin Films Mylar® RSX951 Polyester Film, 140 Gauge
Copyright © lookpolymers.com All Rights Reserved