Techmer ES Elastoblend® PA6/6 GF13 IM2 HS L 13% Glass Filled
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 10% Glass Fiber Filled , Nylon 66, Glass Reinforced, Impact Grade , Nylon 66, Heat Stabilized |
| Manufacturer | Techmer ES |
| Trade Name | Elastoblend® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES Elastoblend® PA6/6 GF13 IM2 HS L 13% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 13% Filler by WeightAdditive: Heat Stabilizer, Lubricant and Impact ModifierFeatures: Heat Stabilized, Lubricant and Impact ModifiedInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | ASTM D792 |
| Water Absorption | 1.1 % @Time 86400 sec |
1.1 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm @Thickness 3.17 mm |
0.0050 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 111 | 111 | ASTM D785 |
| Tensile Strength, Yield | 91.7 MPa | 13300 psi | ASTM D638 |
| Elongation at Break | 4.4 % | 4.4 % | ASTM D638 |
| Flexural Strength | 125 MPa | 18200 psi | ASTM D790 |
| Flexural Modulus | 3.79 GPa | 550 ksi | ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm @Thickness 3.17 mm, Temperature -40.0 °C |
2.00 ft-lb/in @Thickness 0.125 in, Temperature -40.0 °F |
ASTM D256 |
| 1.60 J/cm @Thickness 3.17 mm, Temperature 22.8 °C |
3.00 ft-lb/in @Thickness 0.125 in, Temperature 73.0 °F |
ASTM D256 | |
| Izod Impact, Unnotched | NB @Thickness 3.17 mm |
NB @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 54.0 µm/m-°C | 30.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 249 °C | 480 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 221 °C | 430 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | ASTM D257 |
| Dielectric Strength | 19.3 kV/mm | 490 kV/in | Method A (Short-Time); ASTM D149 |
Users viewing this material also viewed the following:
- ITW Devcon One minuteâ„¢ Epoxy Gel, Amber
- Indium Corp. Indalloy® 84001 Flux #1 Paste Flux containing Ammonium Chloride
- SABIC Innovative Plastics LNP STAT-KON AX06518 ABS
- Tipco Tipcolene® BK 4030 - Carbon Black (40% SAF) Masterbatch in LDPE (Low Density Polyethylene)
- ELASTO UK Dryflex® 602300S SEBS Based Material, Filled Qualities, 30A Hardness, Black
- Clariant Renol PPSSP0006 Polyphenylene Sulfide, Glass Fiber, PTFE Lubricated
- 3M Dyneon™ TFE 90Z Peroxide Cure Perfluoroelastomer
- TSE Industries Millathane® 66 Millable Polyurethane Rubber
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with 60 PHR N220 (ISAF) Filler
Copyright © lookpolymers.com All Rights Reserved