Techmer ES Elastoblend® PA6 GF40 IM2 NAT 40% Glass Filled
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Glass Fiber Filled , Nylon 6, Impact Grade |
| Manufacturer | Techmer ES |
| Trade Name | Elastoblend® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES Elastoblend® PA6 GF40 IM2 NAT 40% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 40% Filler by WeightAdditive: Impact ModifierFeatures: Impact ModifiedUL File Number: E157318Processing Method: Injection MoldingInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.46 g/cc | 0.0527 lb/in³ | ASTM D792 |
| Water Absorption | 0.50 % @Time 86400 sec |
0.50 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.035 cm/cm @Thickness 3.17 mm |
0.035 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Yield | 179 MPa | 25900 psi | ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Strength | 303 MPa | 44000 psi | ASTM D790 |
| Flexural Modulus | 9.65 GPa | 1400 ksi | ASTM D790 |
| Izod Impact, Notched | 1.28 J/cm @Thickness 3.17 mm, Temperature -40.0 °C |
2.40 ft-lb/in @Thickness 0.125 in, Temperature -40.0 °F |
ASTM D256 |
| 2.24 J/cm @Thickness 3.17 mm, Temperature 22.8 °C |
4.20 ft-lb/in @Thickness 0.125 in, Temperature 73.0 °F |
ASTM D256 | |
| Izod Impact, Unnotched | 13.9 J/cm @Thickness 3.17 mm |
26.0 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 36.0 µm/m-°C | 20.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 213 °C | 415 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 2.00e+13 ohm-cm | 2.00e+13 ohm-cm | ASTM D257 |
| Dielectric Strength | 15.4 kV/mm | 390 kV/in | Method A (Short-Time); ASTM D149 |
Users viewing this material also viewed the following:
- Nyco NYGLOS® 20 Wollastonite
- Osprey Metals 316L Stainless Steel Powder (Grade 95% - 16)
- PSM Industries PolyAlloys MIM-Fe-50%Ni Grade 1 Soft Magnetic Steel
- SYNTHOS Krasten® 152 General Purpose Polystyrene
- Shandong Dongyue Shenzhou New Material Co CHF100 Perfluorosulfonic Acid Ion-Exchange Resin (PFSA)
- Schott RG1000 Long Pass Filter
- Saint-Gobain Norton® Fluorglas® Chemfilm® R167 Extruded Expanded PTFE Film (0.006" thick)
- Dow Corning Q3-3559 SEMIFLOWABLE TEXTILE ELASTOMER
- ConocoPhillips Hydroclear® 30 Power-D E.O. 30
Copyright © lookpolymers.com All Rights Reserved