SABIC Innovative Plastics LNP THERMOCOMP NX10302 PC+ABS (Asia Pacific)
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP NX10302 PC+ABS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
This is a PC/ABS compound with improved plating, surface and mechanical performance, a good candidate for Laser Direct Structuring applications.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.26 g/cc | 0.0455 lb/in³ | ASTM D792 |
| Water Absorption | 0.010 % @Time 86400 sec |
0.010 % @Time 24.0 hour |
ASTM D570 |
| Moisture Absorption | 0.0200 % | 0.0200 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0060 - 0.0065 cm/cm @Time 86400 sec |
0.0060 - 0.0065 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0056 cm/cm @Time 86400 sec |
0.0050 - 0.0056 in/in @Time 24.0 hour |
ASTM D955 |
| Melt Index of Compound | 14 g/10 min @Load 5.00 kg, Temperature 260 °C |
14 g/10 min @Load 11.0 lb, Temperature 500 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 47.0 MPa | 6820 psi | Type I, 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 46.0 MPa | 6670 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 100 % | 100 % | Type I, 5 mm/min; ASTM D638 |
| Elongation at Yield | 4.2 % | 4.2 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 2.48 GPa | 360 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 79.0 MPa | 11500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Yield Strength | 80.0 MPa | 11600 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 2.40 GPa | 348 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 6.00 J/cm | 11.2 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | NB | NB | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 84.7 µm/m-°C @Temperature -40.0 - 40.0 °C |
47.1 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 91.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
50.6 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 1.8 MPa (264 psi) | 108 °C @Thickness 3.20 mm |
226 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 2.74 @Frequency 1.00e+9 Hz |
2.74 @Frequency 1.00e+9 Hz |
IEC 60250 |
| Dissipation Factor | 0.0030 @Frequency 1.00e+9 Hz |
0.0030 @Frequency 1.00e+9 Hz |
IEC 60250 |
Users viewing this material also viewed the following:
- Solvay TECHNYL® A 30 H1 V25 PA66, 25% glass fiber, Conditioned
- Samsung Cheil Industries Starex® WR-9120AT ASA, Unreinforced
- DSM Biomedical Elasthane™ 80A Thermoplastic Polyether Polyurethane (TPU)
- Daikin POLYFLON M-139 PTFE Molding Powder, Free Flow
- Aclo Accucomp Polypropylene CPO402V Automotive Approved Copolymer Extrusion Grade
- 3M 9088FL High Performance Double Coated Tapes with Adhesive 375
- BASF N,N-Dimethylisopropanolamine
- Clariant Renol PA111G30IF Nylon 66, 30% Glass Fiber, Improved Flow
- 3M Nextel™ DF-19 Woven Fabric 610
- Bulk Molding Compounds BMC T40(18)-LS Die Casting Replacement Grade Molding Compound
Copyright © lookpolymers.com All Rights Reserved