Sumitomo Bakelite North America FM 1132P Cellulose Reinforced Phenolic Novolac

Category Polymer , Thermoset , Filled/Reinforced Thermoset , Phenolic , Phenolic, Novolac, Cellulose Filled
Manufacturer Sumitomo Bakelite North America
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Sumitomo Bakelite North America FM 1132P Cellulose Reinforced Phenolic Novolac.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
FM 1132P is a two-stage phenolic molding compound reinforced with cellulose in pellet form. FM-1132P is recommended to customers desiring approval under ASTM D-5948-96,Type CFI-10. (Replaces Military Specification MIL-M-14H.)Information supplied by Sumitomo Bak North America.
Physical Properties Metric English Comments
Bulk Density 0.400 g/cc
0.0145 lb/in³
Powder; ASTM D1895
Density 1.37 g/cc
0.0495 lb/in³
ASTM D-792
Water Absorption 0.60 %
0.60 %
24 hour; ASTM D570
Linear Mold Shrinkage 0.0030 cm/cm
0.0030 in/in
ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell E 115
115
ASTM D785
Tensile Strength, Ultimate 45.0 MPa
6530 psi
ASTM D638
Flexural Strength 70.0 MPa
10200 psi
ASTM D790
Flexural Modulus 8.00 GPa
1160 ksi
ASTM D790
Compressive Strength 193 MPa
28000 psi
ASTM D695
Izod Impact, Notched 0.590 J/cm
1.11 ft-lb/in
ASTM D256A
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 150 °C
302 °F
UL Temperature Index; UL 746B
Deflection Temperature at 1.8 MPa (264 psi) 180 °C
356 °F
As Molded; ASTM D648A
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
Electrical Properties Metric English Comments
Dielectric Strength 4.80 kV/mm
122 kV/in
60 Hz, wet, SS; ASTM D149
7.20 kV/mm
183 kV/in
ST; ASTM D149
Descriptive Properties Value Comments
Available Molding Grades Compression, Transfer, Injection
Color Black
Form Pellet