Styron STYRONâ„¢ 6500 Ignition Resistant Polystyrene Resin

Category	Polymer , Thermoplastic , Polystyrene (PS)
Manufacturer	Styron
Trade Name	STYRON™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Styron STYRONâ„¢ 6500 Ignition Resistant Polystyrene Resin.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Overview: STYRONâ„¢ 6500 is an ignition-resistant polystyrene resin with excellent balance of strength, heat resistance and flow properties that are tailor-made for consumer electronics applications. It is a non-decay ignition resistant polystyrene which is free from polybrominated diphenyl ether (PBDPE) and polybrominated biphenyl (PBB). It is designed for injection molding application.Main Characteristics:Good flowExcellent heat resistanceUL 94 V-0 @ 1.5 mmApplications: LCD TV enclosuresInformation provided by Styron

Physical Properties	Metric	English	Comments
Density	1.16 g/cc	0.0419 lb/inÂ³	ASTM D792
Linear Mold Shrinkage, Flow	0.0040 - 0.0070 cm/cm	0.0040 - 0.0070 in/in	ASTM D955
Melt Flow	10 g/10 min @Load 5.00 kg, Temperature 200 Â°C	10 g/10 min @Load 11.0 lb, Temperature 392 Â°F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	13.8 MPa	2000 psi	Compression Molded; ASTM D638
	19.3 MPa	2800 psi	Injection Molded; ASTM D638
Tensile Strength, Yield	17.2 MPa	2490 psi	Compression Molded; ASTM D638
	20.7 MPa	3000 psi	Injection Molded; ASTM D638
Elongation at Break	30 %	30 %	Compression Molded; ASTM D638
	40 %	40 %	Injection Molded; ASTM D638
Flexural Strength	33.8 MPa	4900 psi	Compression Molded; ASTM D790
	40.7 MPa	5900 psi	Injection Molded; ASTM D790
Flexural Modulus	1.99 GPa	289 ksi	Compression Molded; ASTM D790
	2.37 GPa	344 ksi	Injection Molded; ASTM D790
Izod Impact, Notched	0.640 J/cm @Temperature 23.0 Â°C	1.20 ft-lb/in @Temperature 73.4 Â°F	Compression Molded; ASTM D256
	0.800 J/cm @Temperature 23.0 Â°C	1.50 ft-lb/in @Temperature 73.4 Â°F	Injection Molded; ASTM D256

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	76.0 Âµm/m-Â°C	42.2 Âµin/in-Â°F	ASTM D696
Vicat Softening Point	100 Â°C	212 Â°F	ASTM D1525
Flammability, UL94	V-0 @Thickness 1.50 mm	V-0 @Thickness 0.0591 in