- Chosun Refractories RSP-M Blast Furnace Runner Refractory
Chosun Refractories RSP-M Blast Furnace Runner Refractory
| Category | Ceramic , Oxide , Aluminum Oxide |
| Manufacturer | Chosun Refractories |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chosun Refractories RSP-M Blast Furnace Runner Refractory.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Chosun Refractories via Korea Institute of Ceramic Engineering and Technology (KICET).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 2.80 g/cc @Temperature 1500 °C, Time 10800 sec |
0.101 lb/in³ @Temperature 2730 °F, Time 3.00 hour |
|
| 2.84 g/cc @Temperature 110 °C, Time 86400 sec |
0.103 lb/in³ @Temperature 230 °F, Time 24.0 hour |
||
| Porosity | 14.9 % @Temperature 110 °C, Time 86400 sec |
14.9 % @Temperature 230 °F, Time 24.0 hour |
|
| 20 % @Temperature 1500 °C, Time 10800 sec |
20 % @Temperature 2730 °F, Time 3.00 hour |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Rupture | 0.0054936 GPa @Temperature 110 °C, Time 86400 sec |
0.79679 ksi @Temperature 230 °F, Time 24.0 hour |
|
| 0.0084366 GPa @Temperature 1500 °C, Time 10800 sec |
1.2236 ksi @Temperature 2730 °F, Time 3.00 hour |
||
| Compressive Strength | 17.5 MPa @Temperature 110 °C, Time 86400 sec |
2530 psi @Temperature 230 °F, Time 24.0 hour |
Cold Crushing Strength |
| 26.6 MPa @Temperature 1500 °C, Time 10800 sec |
3850 psi @Temperature 2730 °F, Time 3.00 hour |
Cold Crushing Strength |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage | -0.120 % @Temperature 1500 °C, Time 7200 sec |
-0.120 % @Temperature 2730 °F, Time 2.00 hour |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Al2O3 | 72 % | 72 % | |
| MgO | 5.4 % | 5.4 % | |
| SiC | 14 % | 14 % | |
| SiO2 | 2.0 % | 2.0 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Chemical Analysis(%),FC | 2 | |
| Installation Method | Casing Vibrating | |
| Main Applications | Main runner Metal Zone | |
| Material Required for Estimating (kg/?) | 2,900 | |
| Water Required for Casting(%) | 5.7 |
Users viewing this material also viewed the following:
- Plastcom SLOVALEN PQ 83 T 15 PP, 15% mineral filling, UV stabilization
- Pyrotek Wollite 37 Insulating Castable
- Chevron Phillips Marlex® C513UV HDPE Blow Molding Resin (discontinued **)
- Ferro EG 2760 Thick Film Glass
- Ineos ABS Lustran® LGA
- LG Chemical Methyl Acrylate
- DuPont Elvaloy® 3427 AC Ethylene and 27% Butyl Acrylate Copolymer
- BASF Styropor® BFL 222 EPS
- Schmolz + Bickenbach Cryodur® 2767 Cold Work Die Steel
Copyright © lookpolymers.com All Rights Reserved