Styrolution Polystyrol ESCRimo PS
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Impact Modified |
| Manufacturer | Styrolution |
| Trade Name | Polystyrol |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styrolution Polystyrol ESCRimo PS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Polystyrol ESCRimo is a high-impact polystyrene grade with an improved stress cracking resistance compared to conventional high-impact polystyrene.Applications: Due to its superior environmental stress cracking resistance Polystyrol ESCRimo is in particular suitable for the refrigeration segment (inliner and doorliner). Because of its improved chemical resistance Polystyrol ESCRimo can also be used in food packaging applications.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.029 g/cc | 0.03717 lb/in³ | ISO 1183 |
| Water Absorption | <= 0.10 % | <= 0.10 % | ISO 62 |
| Moisture Absorption at Equilibrium | <= 0.10 % | <= 0.10 % | 23°C/50% RH; ISO 62 |
| Melt Flow | 3.602 g/10 min @Load 5.00 kg, Temperature 200 °C |
3.602 g/10 min @Load 11.0 lb, Temperature 392 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 22.0 MPa | 3190 psi | 50 mm/min; ISO 527-1/-2 |
| Elongation at Break | 50 % | 50 % | Nominal, 50mm/min; ISO 527-1/-2 |
| Elongation at Yield | 1.8 % | 1.8 % | 50 mm/min; ISO 527-1/-2 |
| Tensile Modulus | 1.50 GPa | 218 ksi | ISO 527-1/-2 |
| Charpy Impact Unnotched | <= 14.0 J/cm² @Temperature -30.0 °C |
<= 66.6 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| <= NB @Temperature 23.0 °C |
<= NB @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.700 J/cm² @Temperature -30.0 °C |
3.33 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 1.50 J/cm² @Temperature 23.0 °C |
7.14 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 87.0 °C | 189 °F | VST/B/50; ISO 306 |
| Flammability, UL94 | HB @Diameter 1.60 mm |
HB @Diameter 0.0630 in |
IEC 60695-11-10 |
| HB @Diameter 3.20 mm |
HB @Diameter 0.126 in |
IEC 60695-11-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+16 ohm-cm | >= 1.00e+16 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+13 ohm | >= 1.00e+13 ohm | IEC 60093 |
| Dielectric Constant | 2.5 @Frequency 100 Hz |
2.5 @Frequency 100 Hz |
IEC 60250 |
| Dielectric Strength | 155 kV/mm | 3940 kV/in | K20/P50; IEC 60243-1 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 200 - 230 °C | 392 - 446 °F | Plates |
| 180 - 260 °C | 356 - 500 °F | Injection molding | |
| 200 - 240 °C | 392 - 464 °F | Flat film | |
| Mold Temperature | 10.0 - 60.0 °C | 50.0 - 140 °F | Injection Molding |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Natural | |
| Commercial Status | Europe | |
| Primary Processing Technique | Injection Molding and Extrusion | |
| Surface Gloss | 10 | Skalenteile |
Users viewing this material also viewed the following:
- MV Labs CR800 Cr2O3 Chromium(III) oxide
- Nye Lubricants UniFlor 8512F (842G0) (UF) Synthetic Oil
- Ovation Polymers Opnyl OP6GF43 Nylon 6, 43% Glass Reinforced, Dry
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 20 PHR Non-Black, Aerosil 200
- Techmer ES Luriblend® PA6 TS18 Nylon 6
- SABIC Innovative Plastics LNP THERMOCOMP GX05482 PSU (Asia Pacific)
- Hexcel® HexPly® ES70 120°C Curing Epoxy Matrix, E-glass UD fabric 430 g/m2
- Polyram RamLloy PA917G6 PP/NYLON 66 alloy, 30% Glass Fiber
- ChevronTexaco ISO 100 Utility Oil HVI
Copyright © lookpolymers.com All Rights Reserved