Stratasys® PC-ABS
| Category | Polymer , Rapid Prototyping Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | Stratasys |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Stratasys® PC-ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PC-ABS (polycarbonate-ABS) is one of the most widely used industrial thermoplastics. PC-ABS offers the most desirable properties of both materials - the superior mechanical properties and heat resistance of PC and the excellent features of ABS. PC-ABS blends are commonly used in automotive, electronics and telecommunications applications. When combined with Stratasys FDM (Fused Deposition Modeling) systems, PC-ABS gives you Real Parts™ for conceptual prototyping through design verification through direct digital manufacturing.Information provided by Stratasys®
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 110 | 110 | ASTM D785 |
| Tensile Strength, Ultimate | 34.8 MPa | 5050 psi | Type 1, 2"/min; ASTM D638 |
| Elongation at Break | 4.3 % | 4.3 % | ASTM D638 |
| Tensile Modulus | 1.827 GPa | 265.0 ksi | Type 1, 2"/min; ASTM D638 |
| Flexural Strength | 50.0 MPa | 7250 psi | ASTM D790 |
| Flexural Modulus | 1.863 GPa | 270.2 ksi | ASTM D790 |
| Izod Impact, Notched | 1.23 J/cm | 2.30 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.26 J/cm | 6.11 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 73.8 µm/m-°C @Temperature 20.0 °C |
41.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C | 230 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 96.0 °C | 205 °F | ASTM D648 |
| Vicat Softening Point | 112 °C | 234 °F | ASTM D1525 |
| Glass Transition Temp, Tg | 125 °C | 257 °F | DSC (SSYS) |
| Flammability, UL94 | HB @Thickness 0.850 mm |
HB @Thickness 0.0335 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 3.0 @Frequency 1.00e+6 Hz |
3.0 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.1 @Frequency 60.0 Hz |
3.1 @Frequency 60.0 Hz |
IEC 60250 | |
| Dielectric Strength | 35.0 kV/mm | 889 kV/in | IEC 60112 |
Users viewing this material also viewed the following:
- Hong Kun Group DIC Pharmaceutical Intermediate
- ThyssenKrupp N-A-XTRA® 550 Structural Steel
- Wellman Wellamid® GFT33N051-NBK2 Nylon 66, 33% Glass Fiber Reinforced, Impact Modified
- A. Schulman POLYFORT™ FPP 1285U Glass Filled, UV Stable Impact Copolymer Polypropylene
- A. Schulman POLYBATCH™ XU-2013-LD Concentrate Based In LDPE
- A. Schulman POLYBATCH™ Light Grey 80426U Concentrate Based In LLDPE
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 30 PHR Suprex Clay Filler
- ConocoPhillips Syncon® 68 Synthetic AW Hydraulic Fluid 68
- ATI Allvac® VascoMax® T-250 Specialty Steel, Heat Treatment: 816°C (1500°F) + Age
Copyright © lookpolymers.com All Rights Reserved