Special Metals NIMONIC® Alloy PE16
| Category | Metal , Nonferrous Metal , Nickel Alloy , Superalloy |
| Manufacturer | Special Metals (includes the former Inco Alloys International Inc.) |
| Trade Name | NIMONIC® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Special Metals NIMONIC® Alloy PE16.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
A precipitation-hardenable nickel-iron-chromium alloy with an addition of molybdenum for solid-solution strengthening. It has good strength and oxidation resistance at temperatures to about 1380°F (750°C). The alloy is designed to provide a precipitation-hardened material having excellent hot-working, cold-working, and welding characteristics. Used for gas-turbine components and in nuclear reactors. Standard product forms are round, flats, extruded section, sheet, strip, tube, and wire.Data provided by the manufacturer, Special Metals.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 8.02 g/cc | 0.290 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 720 MPa @Temperature 550 °C |
104000 psi @Temperature 1020 °F |
Precipitation Hardened prior to test |
| 900 MPa @Temperature 23.0 °C |
131000 psi @Temperature 73.4 °F |
||
| Tensile Strength, Yield | 450 MPa @Strain 0.200 % |
65300 psi @Strain 0.200 % |
Precipitation Hardened. Value at room temperature |
| 380 MPa @Strain 0.200 %, Temperature 550 °C |
55100 psi @Strain 0.200 %, Temperature 1020 °F |
Precipitation Hardened prior to test | |
| Elongation at Break | 28 % | 28 % | Precipitation Hardened |
| 30 % @Temperature 550 °C |
30 % @Temperature 1020 °F |
Precipitation Hardened prior to test. |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 13.8 µm/m-°C @Temperature 20.0 - 100 °C |
7.67 µin/in-°F @Temperature 68.0 - 212 °F |
|
| Specific Heat Capacity | 0.544 J/g-°C | 0.130 BTU/lb-°F | |
| Thermal Conductivity | 11.72 W/m-K | 81.34 BTU-in/hr-ft²-°F | |
| Melting Point | 1310 - 1355 °C | 2390 - 2471 °F | |
| Solidus | 1310 °C | 2390 °F | |
| Liquidus | 1355 °C | 2471 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Aluminum, Al | 1.1 - 1.3 % | 1.1 - 1.3 % | |
| Boron, B | <= 0.0050 % | <= 0.0050 % | |
| Carbon, C | 0.040 - 0.080 % | 0.040 - 0.080 % | |
| Chromium, Cr | 15.5 - 17.5 % | 15.5 - 17.5 % | |
| Cobalt, Co | <= 2.0 % | <= 2.0 % | |
| Copper, Cu | <= 0.50 % | <= 0.50 % | |
| Iron, Fe | 31 % | 31 % | As remainder |
| Manganese, Mn | <= 0.20 % | <= 0.20 % | |
| Molybdenum, Mo | 2.8 - 3.8 % | 2.8 - 3.8 % | |
| Nickel, Ni | 42 - 45 % | 42 - 45 % | Including Cobalt |
| Silicon, Si | <= 0.50 % | <= 0.50 % | |
| Sulfur, S | <= 0.015 % | <= 0.015 % | |
| Titanium, Ti | 1.1 - 1.3 % | 1.1 - 1.3 % | |
| Zirconium, Zr | 0.020 - 0.040 % | 0.020 - 0.040 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.000110 ohm-cm | 0.000110 ohm-cm | |
| Magnetic Permeability | 1.4 | 1.4 | at 200 oersted (15.9 kA/m) |
Users viewing this material also viewed the following:
- Pyrotek SP-160 Refractory Coating
- Lehmann & Voss LUVOCOM® 80-8387/EM Polyacetal-copolymer, unreinforced
- Lord Adhesives 7542D Two-Component Urethane Adhesive
- Teknor Apex Sinpolene MBW001LE Low Density Polyethylene
- Cytec Thornel® P-25 2K Carbon Fiber, Pitch Precursor
- Chicago Extruded Metals BioBrass® UNS C26000 Copper-Zinc Alloy
- Asahi Kasei Tenac® SH710 Homopolymer Acetal Resin
- 3M 9172MP High Performance Adhesive Transfer Tapes with Adhesive 200MP
- Radici Radilon® A CF350 (cond.) Nylon 66
- Grupo Repol Dinalon® B1X25 HI PA6 High Impact
Copyright © lookpolymers.com All Rights Reserved