Special Metals MONEL® 404 Copper-Nickel Alloy
| Category | Metal , Nonferrous Metal , Nickel Alloy |
| Manufacturer | Special Metals (includes the former Inco Alloys International Inc.) |
| Trade Name | MONEL® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Special Metals MONEL® 404 Copper-Nickel Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by California Fine Wire and the manufacturer, Special Metals.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 8.91 g/cc | 0.322 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 483 MPa | 70000 psi | Annealed |
| 655 MPa | 95000 psi | Stress relieved | |
| 758 MPa | 110000 psi | Hard | |
| Tensile Strength, Yield | 172 MPa | 25000 psi | Annealed |
| 517 MPa | 75000 psi | Stress relieved | |
| 689 MPa | 100000 psi | Hard | |
| Modulus of Elasticity | 169 GPa | 24500 ksi | |
| Poissons Ratio | 0.295 | 0.295 | |
| Shear Modulus | 65.0 GPa | 9430 ksi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 13.3 µm/m-°C @Temperature 21.0 - 93.0 °C |
7.39 µin/in-°F @Temperature 69.8 - 199 °F |
Mean |
| 15.3 µm/m-°C @Temperature 21.0 - 300 °C |
8.50 µin/in-°F @Temperature 69.8 - 572 °F |
Mean | |
| 16.6 µm/m-°C @Temperature 21.0 - 538 °C |
9.22 µin/in-°F @Temperature 69.8 - 1000 °F |
Mean | |
| 17.6 µm/m-°C @Temperature 21.0 - 815 °C |
9.78 µin/in-°F @Temperature 69.8 - 1500 °F |
Mean | |
| Specific Heat Capacity | 0.414 J/g-°C | 0.0989 BTU/lb-°F | |
| Melting Point | 1300 °C | 2370 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Aluminum, Al | <= 0.050 % | <= 0.050 % | |
| Carbon, C | <= 0.15 % | <= 0.15 % | |
| Copper, Cu | <= 45.5 % | <= 45.5 % | As remainder |
| Iron, Fe | <= 0.50 % | <= 0.50 % | |
| Manganese, Mn | <= 0.10 % | <= 0.10 % | |
| Nickel, Ni | 52 - 57 % | 52 - 57 % | Including Cobalt |
| Silicon, Si | <= 0.10 % | <= 0.10 % | |
| Sulfur, S | 0.024 % | 0.024 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.0000500 ohm-cm | 0.0000500 ohm-cm | |
| Magnetic Permeability | 1.0017 | 1.0017 | 200 Oersted; Annealed and Furnace-cooled |
| 1.0047 | 1.0047 | at 200 Oersted; As-Forged | |
| Curie Temperature | <= -85.0 °C | <= -121 °F | As-Forged |
| <= -79.0 °C | <= -110 °F | Annealed and Furnace-cooled |
Users viewing this material also viewed the following:
- RheTech Products FT3150-01 Thermoplastic Polyolefin, Non-UV Stabilized, Black
- Precision Polymer Engineering V75P Fluoroelastomer Compound
- PolyOne Geon™ Vinyl Flexible A85UB Polyvinyl Chloride, Flexible (PVC, Flexible)
- ITW Devcon Plastic Welderâ„¢ Methacrylate Adhesive II, Straw, Black
- Momentive Performance Materials SS4171P Addition Cure Silicone Rubber Molding Compounds
- SABIC Innovative Plastics NORYL EFN4230 PPE+PS (Asia Pacific)
- Trelleborg AEM Eccofloat® TG-24/2000 Syntactic Foam
- Cheng Yu Plastic T882GV1 Flame Retardant PBT, 10% Glass Fiber
- Solvay Specialty Polymers Ryton® PR11 Polyphenylene Sulfide Resin (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved