Special Metals BRIGHTRAY® Alloy 35 Electrical Resistance Alloy
| Category | Metal , Electronic/Magnetic Alloy , Superalloy , Iron Base |
| Manufacturer | Special Metals (includes the former Inco Alloys International Inc.) |
| Trade Name | BRIGHTRAY® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Special Metals BRIGHTRAY® Alloy 35 Electrical Resistance Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
A nickel-iron-chromium electrical-resistance alloy for use at operating temperatures up to 1920°F (1050°C). It is similar to BRIGHTRAY alloy F but with rare-earth additions for greater resistance to oxidation under conditions of frequent switching or wide temperature fluctuations. The alloy has a high temperature coefficient of resistance. Used for heating elements in domestic appliances and industrial equipment. The standard product form is wire.Data provided by the manufacturer, Special Metals.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 7.93 g/cc | 0.286 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 610 MPa | 88500 psi | Annealed prior to test |
| 500 MPa @Temperature 550 °C |
72500 psi @Temperature 1020 °F |
Annealed prior to test | |
| Tensile Strength, Yield | 250 MPa @Strain 0.200 % |
36300 psi @Strain 0.200 % |
Annealed prior to test |
| 140 MPa @Strain 0.200 %, Temperature 550 °C |
20300 psi @Strain 0.200 %, Temperature 1020 °F |
Annealed prior to test |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 12.9 µm/m-°C @Temperature 20.0 - 100 °C |
7.17 µin/in-°F @Temperature 68.0 - 212 °F |
|
| Specific Heat Capacity | 0.523 J/g-°C | 0.125 BTU/lb-°F | |
| Melting Point | 1340 - 1380 °C | 2440 - 2520 °F | |
| Solidus | 1340 °C | 2440 °F | |
| Liquidus | 1380 °C | 2520 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Carbon, C | <= 0.15 % | <= 0.15 % | |
| Chromium, Cr | 18 - 21 % | 18 - 21 % | |
| Iron, Fe | 42 % | 42 % | As remainder |
| Manganese, Mn | <= 1.0 % | <= 1.0 % | |
| Nickel, Ni | 34 - 37 % | 34 - 37 % | Including Cobalt |
| Silicon, Si | 1.0 - 3.0 % | 1.0 - 3.0 % | |
| Sulfur, S | <= 0.010 % | <= 0.010 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.000102 ohm-cm | 0.000102 ohm-cm | Temperature coefficient of resistance is 330 µOhm/Ohm-°C in the range 25-500°C. |
| Magnetic Permeability | 1.026 | 1.026 | at 200 oersted (15.9 kA/m) |
Users viewing this material also viewed the following:
- Multibase SILASTIC® C7-4550 TBPB Dow-Corning Biomedical Grade ETR Elastomer
- Daelim H&L Plavis G15 Aromatic Polyimide, 15% Graphite Filled, Direct Formed (Unverified Data**)
- Hong Kun Group UV 1130 UV Absorber
- Mateck MgO
- Wanhua Chemical Wanthane® WHT-6290 TPU Hot-Melt Adhesive
- Zircar Ceramics HC Sapphire (Single Crystal Aluminum Oxide) Hangar Clip
- Cytec (Conap) RN-1210 / EA-87 Conapoxy® Resin / Conacure® Hardener
- Eurostar Staramide ACF2 PA66, 10% Carbon Fiber Reinforced, Heat stabilized, Injection Molding
- AorTech Biomaterials ECSil™ 70D Biomedical Carbonate Silicone Pellets
Copyright © lookpolymers.com All Rights Reserved