Spartech PP5140 Talc Filled Homopolymer
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 40% Talc Filler |
| Manufacturer | Spartech |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Spartech PP5140 Talc Filled Homopolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Offers an excellent balance of processing improvement and high levels of stiffness and heat deflection temperatureInformation provided by Spartech
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.25 g/cc @Temperature 22.8 °C |
1.25 g/cc @Temperature 73.0 °F |
ASTM D792 |
| Filler Content | 40 % | 40 % | |
| Linear Mold Shrinkage | 0.010 cm/cm | 0.010 in/in | 0.125inch wall |
| 0.012 cm/cm | 0.012 in/in | 4.0" disk; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 31.0 MPa | 4500 psi | ASTM D638 |
| Elongation at Break | 10 % | 10 % | ASTM D638 |
| Elongation at Yield | 2.0 % | 2.0 % | ASTM D638 |
| Flexural Modulus | 2.41 GPa | 350 ksi | secant; ASTM D790 |
| 3.17 GPa | 460 ksi | tangent; ASTM D790 | |
| Izod Impact, Notched | 0.267 J/cm @Temperature 22.8 °C |
0.500 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Gardner Impact | >= 1.36 J @Temperature 22.8 °C |
>= 1.00 ft-lb @Temperature 73.0 °F |
ASTM D5420 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 172 µm/m-°C @Temperature 20.0 °C |
95.6 µin/in-°F @Temperature 68.0 °F |
ASTM E831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C | 275 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 79.4 °C | 175 °F | ASTM D648 |
| Vicat Softening Point | 84.0 °C | 183 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | 20 % | 20 % | 60°; ASTM D523 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 4.8 @Frequency 60 Hz |
4.8 @Frequency 60 Hz |
ASTM D150 |
| Dielectric Strength | 19.7 kV/mm | 500 kV/in | ASTM D149 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Drying Temperature | 82.0 - 104 °C | 180 - 219 °F | |
| Dry Time | 4 - 6 hour | 4 - 6 hour | to moisture < 0.01% |
Users viewing this material also viewed the following:
- NYCOA ASN 27 300 KNF 30% Glass Fiber Reinforced, Heat Stabilized Nylon 6 Resin
- SABIC Innovative Plastics Cycoloy® IP1000 PC+ABS (Asia Pacific)
- Parker Chomerics CHO-SORB® EMI Ferrites
- Menzolit Menzolit® SMC 0650 Unsaturated Polyester UP
- Industeel SIRIUS 800 H+ Heat Resistant Alloy
- Saint-Gobain CHR® 2829-3(R) Acrylic Adhesive Zone Tape
- ConocoPhillips Syncon® 460 Synthetic R&O Oil
- Ashley Polymers Ashlene® T940H Nylon 11
- LNP Lubricomp® PDX-O-88533 BK8-229 Polyphenylene Sulfide, Glass Fiber Reinforcement, PTFE Lubricant (disconti
Copyright © lookpolymers.com All Rights Reserved