- Solvay TECHNYL® A 20 V35 PA66, 35% glass fiber, Conditioned
Solvay TECHNYL® A 20 V35 PA66, 35% glass fiber, Conditioned
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Glass Fiber Filled |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYL® A 20 V35 PA66, 35% glass fiber, Conditioned.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Flame retardant polyamide 66, reinforced with 35% of glass fiber, for injection molding.Available in: Asia Pacific, Europe, Latin America and North America.Product Applications: This phosphorous flame retardant grade, UL 94 V0 (0.8 mm), offers excellent filling qualities and with good mechanical properties. This grade is suitable for molding insulating parts for electrical devices: connectors, switches, bobbins coil formers and thin parts under stress. This product is available in black.Information provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.46 g/cc | 0.0527 lb/in³ | ISO 1183/A |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 140 MPa | 20300 psi | ISO 527 Type 1A |
| Tensile Strength, Yield | 140 MPa | 20300 psi | ISO 527 type 1 A |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527 Type 1A |
| Elongation at Yield | 3.0 % | 3.0 % | ISO 527 type 1 A |
| Tensile Modulus | 10.0 GPa | 1450 ksi | ISO 527 Type 1A |
| Flexural Strength | 200 MPa | 29000 psi | ISO 178 |
| Flexural Modulus | 7.50 GPa | 1090 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 12.0 kJ/m² | 5.71 ft-lb/in² | ISO 180/1A |
| Charpy Impact Unnotched | 7.00 J/cm² | 33.3 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 1.20 J/cm² | 5.71 ft-lb/in² | ISO 179/1eA |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+11 ohm | 1.00e+11 ohm | IEC 60093 |
| Dielectric Strength | 25.0 kV/mm | 635 kV/in | IEC 60243 |
| Dissipation Factor | 0.050 | 0.050 | IEC 60250 |
| Comparative Tracking Index | 375 V | 375 V | Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Moisture Content | <= 0.20 % | <= 0.20 % |
Users viewing this material also viewed the following:
- Plaskolite Optix® CA - 51 FDA General Purpose Acrylic Resin
- MV Labs CO735 [Co(C2H8N2)3](NO3)3 Tris(ethylenediamine)cobalt(III) nitrate
- Premix Thermoplastics PRE-ELEC® ESD 5350 Static Dissipative Thermoplastic Compound
- Ravago Manufacturing Americas Hylex® P1310LLT Polycarbonate
- Radici Heraflex® A 70-21-22 TPS-SEBS Thermoplastic Elastomer
- LyondellBasell Montell 1900H UHMW Polyethylene
- LyondellBasell Alathon® M6138 High Density Polyethylene
- Kotec Carbotex KGN-30MRA Polycarbonate, Flame Retardant, 30% Glass Fiber Reinforced
- SABIC Innovative Plastics Noryl MX5569 PPE+PS
- E-Polymers SEPAZ® N1040 Nanoclay 4% High Flow Nano Composite Resin
Copyright © lookpolymers.com All Rights Reserved