Solvay Specialty Polymers Torlon® 4601 Polyamide-imide (PAI)
| Category | Polymer , Thermoplastic , Polyamide-imide (PAI) , Polyamide-Imide, Extruded |
| Manufacturer | Solvay Specialty Polymers |
| Trade Name | Torlon® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Specialty Polymers Torlon® 4601 Polyamide-imide (PAI).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Torlon® 4601 is a specialty wear-resistant grade of polyamide-imide (PAI). Most Torlon® PAI grades cannot be molded successfully in molds with undercuts. Torlon® 4601 has been formulated to be moldable in tools with minor undercuts and give very good performance in lubricated wear applications. Features: Flame Retardant; Good Chemical Resistance; Good Creep Resistance; Good Wear Resistance; High Heat Resistance; High Temperature StrengthUses: Bearings; Industrial ApplicationsInformation provided by Solvay Specialty Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.39 g/cc | 0.0502 lb/in³ | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 121 MPa | 17500 psi | ASTM D638 |
| Elongation at Break | 4.1 % | 4.1 % | ASTM D638 |
| Tensile Modulus | 4.21 GPa | 611 ksi | ASTM D638 |
| Flexural Strength | 182 MPa | 26400 psi | ASTM D790 |
| Flexural Modulus | 4.48 GPa | 650 ksi | ASTM D790 |
| Shear Strength | 108 MPa | 15700 psi | ASTM D732 |
| Izod Impact, Notched | 2.30 J/cm | 4.31 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.70 J/cm | 6.93 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 284 °C | 543 °F | Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 304 °C | 579 °F | |
| Nozzle Temperature | 371 °C | 700 °F | |
| Mold Temperature | 199 - 216 °C | 390 - 421 °F | |
| Drying Temperature | 177 °C @Time 10800 sec |
351 °F @Time 3.00 hour |
|
| Moisture Content | <= 0.050 % | <= 0.050 % | |
| Back Pressure | 6.89 MPa | 999 psi | |
| Screw Speed | 50 - 100 rpm | 50 - 100 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| Latin America | ||
| North America | ||
| Form | Pellets | |
| Processing Technique | Injection Molding; Machining; Profile Extrusion | |
| Screw L/D Ratio | 18.0:1.0 to 24.0:1.0 |
Users viewing this material also viewed the following:
- Nilit FRIANYL B63 W-GV35 Nylon 6 for injection molding, 35% glass fiber reinforced
- Inno-Comp INNOPOL® CS 3-3120 B 20% Talc-Filled Polypropylene
- Westlake EF403 Low Density Polyethylene
- Wieland Auropal 1 Casting Alloy
- A. Schulman POLYBATCH™ White LL8855 GP Concentrate Based In LLDPE
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 30 PHR N330 Filler
- Eagle Brass 706 Copper Nickel 10%, Extra Hard
- 3M Scotchcal™ ElectroCut™ 7725-24 Graphic Film
- 3M 9576B Splicing Tape
- PolyOne Synprene® RT-3720 Thermoplastic Elastomer - SBC, Mineral Filled (discontinued **)
Copyright © lookpolymers.com All Rights Reserved