- Solvay Specialty Polymers Solef® 41308 Polyvinylidene Fluoride (PVDF)
Solvay Specialty Polymers Solef® 41308 Polyvinylidene Fluoride (PVDF)
| Category | Polymer , Thermoplastic , Fluoropolymer , PVDF , Polyvinylidinefluoride (PVDF), Molded/Extruded |
| Manufacturer | Solvay Specialty Polymers |
| Trade Name | Solef® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Specialty Polymers Solef® 41308 Polyvinylidene Fluoride (PVDF).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Solef® 41308/0001 PVDF is specifically developed for coextrusion.Additional Properties: Crystallization Heat - ASTM D3418 51.6 J/g; Heat of Fusion - ASTM D3418 52.7 J/gInformation provided by Solvay Specialty Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.78 g/cc | 0.0643 lb/in³ | ISO 1183 |
| Water Absorption | <= 0.040 % @Time 86400 sec |
<= 0.040 % @Time 24.0 hour |
ISO 62 |
| Melt Flow | 6.0 - 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
6.0 - 8.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| 18 - 24 g/10 min @Load 5.00 kg, Temperature 230 °C |
18 - 24 g/10 min @Load 11.0 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 30.0 MPa | 4350 psi | 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 48.0 MPa | 6960 psi | 50 mm/min; ASTM D638 |
| Elongation at Yield | 7.0 % | 7.0 % | 50 mm/min; ASTM D638 |
| Tensile Modulus | 1.90 GPa | 276 ksi | 1.0 mm/min; ASTM D638 |
| Charpy Impact, Notched | 0.850 J/cm² | 4.04 ft-lb/in² | ISO 179 |
| Coefficient of Friction, Dynamic | 0.31 | 0.31 | vs. Itself; ASTM D1894 |
| Coefficient of Friction, Static | 0.32 | 0.32 | vs. Itself; ASTM D1894 |
| Taber Abrasion, mg/1000 Cycles | 8.0 | 8.0 | CS-10 Wheel, 1000 g; ASTM D1044 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 169 °C | 336 °F | DSC |
| Crystallization Temperature | 136 °C | 277 °F | Peak; ASTM D3418 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+14 ohm-cm | >= 1.00e+14 ohm-cm | ASTM D257 |
| Surface Resistance | >= 1.00e+14 ohm | >= 1.00e+14 ohm | ASTM D257 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| Latin America | ||
| North America | ||
| Processing Technique | Coextrusion |
Users viewing this material also viewed the following:
- NYC YT3CP Y2O3 Powder
- PolyOne Geon™ HC 2160G Polyvinyl Chloride, Flexible (PVC, Flexible)
- Fiberfil® J-60/20/E4 Polypropylene Homopolymer, 20% Glass Reinforced, Chemically coupled
- EMS-Grivory Grivory® GM-4H PA*-MD40
- Dow Nordel® NDR 47130.01 EPDM Hydrocarbon Rubber
- Dow Corning 3-6891 1-PART SILICONE RUBBER ABRADABLE SEALANT COMPOUND
- 3M AC-350 Class B-12 Aerospace Sealant
- 3M Scotchcal™ 8000-15 Graphic Film
- Arlon 44981R015 0.015" (0.381 mm) Uncured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved