- Solvay Specialty Polymers Solef® 1015 Polyvinylidene Fluoride (PVDF)
Solvay Specialty Polymers Solef® 1015 Polyvinylidene Fluoride (PVDF)
| Category | Polymer , Thermoplastic , Fluoropolymer , PVDF , Polyvinylidinefluoride (PVDF), Molded/Extruded |
| Manufacturer | Solvay Specialty Polymers |
| Trade Name | Solef® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Specialty Polymers Solef® 1015 Polyvinylidene Fluoride (PVDF).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Solef® 1015 PVDF homopolymer has very high viscosity, suitable for membrane manufacturing. It is available exclusively as powder.Features: Homopolymer; Ultra High ViscosityUses: MembranesAdditional Properties: Crystallization Heat - ASTM D3417 50.0 to 56.0 J/g; Heat of Fusion - ASTM D3417 57.0 to 66.0 J/gInformation provided by Solvay Specialty Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.75 - 1.80 g/cc | 0.0632 - 0.0650 lb/in³ | ASTM D792 |
| Water Absorption | <= 0.040 % @Time 86400 sec |
<= 0.040 % @Time 24.0 hour |
ISO 62 |
| Melt Flow | 2.8 - 4.6 g/10 min @Load 21.6 kg, Temperature 230 °C |
2.8 - 4.6 g/10 min @Load 47.6 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 35.0 - 50.0 MPa @Thickness 2.00 mm |
5080 - 7250 psi @Thickness 0.0787 in |
50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 53.0 - 57.0 MPa @Thickness 2.00 mm |
7690 - 8270 psi @Thickness 0.0787 in |
50 mm/min; ASTM D638 |
| Elongation at Break | 20 - 50 % | 20 - 50 % | 50 mm/min; ASTM D638 |
| Elongation at Yield | 5.0 - 10 % | 5.0 - 10 % | 50 mm/min; ASTM D638 |
| Tensile Modulus | 2.10 - 2.30 GPa | 305 - 334 ksi | 1.0 mm/min; ASTM D638 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 171 - 175 °C | 340 - 347 °F | DSC |
| Crystallization Temperature | 137 - 144 °C | 279 - 291 °F | Peak; ASTM D3418 |
| Glass Transition Temp, Tg | -40.0 °C | -40.0 °F | ASTM E1356 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| Latin America | ||
| North America | ||
| Form | Powder |
Users viewing this material also viewed the following:
- NIZHNEKAMSKNEFTEKHIM 585 General Purpose Polystyrene
- LTL Color Compounds ColorRxâ„¢ PP2-1001A Antimicrobial Polypropylene Random Copolymer
- Gromax BTG30-FN03N1 Nylon 6 30% Glass Filled (Dry)
- Teknor Apex Monprene® MP-1736R1 Thermoplastic Elastomer
- Suqian Unitechem Hindered Amine Light Stabilizer 783
- Zotefoams Plastazote® LD15IC Low Density Polyethylene Foam, Intermediate Cell
- BASF Novolen® 1040 N Polypropylene
- BASF Ultramid® 8200 HS PA 6 (Dry)
- DuPont Elvax® 3173SHB Ethylene-Vinyl Acetate Copolymer Resin for Coextrusion, Blown Film (discontinued **)<
Copyright © lookpolymers.com All Rights Reserved