- PolyOne Stat-Tech™ PK-30NCF/10T PEEK - 30% Nickel Coated Carbon Fiber - 10% PTFE (discontinued **)
PolyOne Stat-Tech™ PK-30NCF/10T PEEK - 30% Nickel Coated Carbon Fiber - 10% PTFE (discontinued **)
| Category | Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Stat-Tech™ PK-30NCF/10T PEEK - 30% Nickel Coated Carbon Fiber - 10% PTFE
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by PolyOne.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.58 g/cc | 1.58 g/cc | ASTM D792 |
| Water Absorption | 0.0010 % @Thickness 3.17 mm |
0.0010 % @Thickness 0.125 in |
24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0010 - 0.0020 cm/cm | 0.0010 - 0.0020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 176 MPa | 25500 psi | Type 1 - Rigids, Yield, 0.2 in/min; ASTM D638 |
| Elongation at Break | 1.0 - 3.0 % | 1.0 - 3.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 11.7 GPa | 1700 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 228 MPa | 33000 psi | ASTM D790 |
| Flexural Modulus | 11.7 GPa | 1700 ksi | ASTM D790 |
| Izod Impact, Notched | 0.747 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
1.40 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 282 °C | 540 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 271 °C | 520 °F | Unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.0 - 10 ohm-cm | 1.0 - 10 ohm-cm | ASTM D257 |
| Surface Resistivity per Square | 1.0 - 10 ohm | 1.0 - 10 ohm | ASTM D257 |
| Shielding Effectiveness | 60 - 70 dB | 60 - 70 dB | 1,000 MHz; PolyOne Internal |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 399 - 427 °C | 750 - 800 °F | Molding |
Users viewing this material also viewed the following:
- Nilit FRIANYL A63 W-GV10 Nylon 6.6 for injection molding, 10% glass fiber reinforced
- BASF Capron® 8200 NL Nylon 6 (Conditioned) (discontinued **)
- H.C. Starck Amperit® 559.074 Agglomerated, Sintered Tungsten Carbide-Cobalt-Chromium 86-6-8 (WC-Co-Cr)
- Lehmann & Voss LUVOCOM® 1-1129 Polyamide 66, with glass fiber, PTFE, lubricant modified, heat stabilized
- Techmer ES HiFill FR® PA6/6 GF40 FR HS L 40% Glass Filled
- A. Schulman POLYFORT™ FPP 3715 Glass Filled Homopolymer Polypropylene
- Hexcel® HexPly® 954-2A Curing Cyanate Resin
- Arkema Group Rilsan® AZM 30 NOIR T6LD Nylon 12, 30% Glass Fiber Filled (Conditioned)
- BASF Elastollan 1154 D FHF TPUR Flame Retardant Halogen Free
- Arkema Group Rilsan® Clear G350 Polyamide
Copyright © lookpolymers.com All Rights Reserved