Solvay Specialty Polymers RytonÂ® R-7-121BL Polyphenylene Sulfide (PPS), GlassMineral Filled

Category	Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS), Mineral/Glass-Fiber Filled
Manufacturer	Solvay Specialty Polymers
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Solvay Specialty Polymers RytonÂ® R-7-121BL Polyphenylene Sulfide (PPS), GlassMineral Filled.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

RytonÂ® R-7-121NA and R-7-121BL glass fiber and mineral filled polyphenylene sulfide compounds provide good mechanical strength with good flow and low maintenance molding using conventional molding equipment.Features: Good Flow; Good StrengthInformation provided by Solvay Specialty Polymers.

Physical Properties	Metric	English	Comments
Density	1.95 g/cc	0.0704 lb/inÂ³	ASTM D792
Water Absorption	0.020 % @Time 86400 sec	0.020 % @Time 24.0 hour	ISO 62
Linear Mold Shrinkage, Flow	0.0020 cm/cm @Thickness 3.18 mm	0.0020 in/in @Thickness 0.125 in
Linear Mold Shrinkage, Transverse	0.0040 cm/cm @Thickness 3.20 mm	0.0040 in/in @Thickness 0.126 in	ASTM D955

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell M	101	101	ASTM D785
Hardness, Rockwell R	118	118	ASTM D785
Tensile Strength	117 MPa	17000 psi	ASTM D638
Tensile Stress	125 MPa	18100 psi	ISO 527-2
Elongation at Break	0.90 %	0.90 %	ISO 527-2
	0.90 %	0.90 %	ASTM D638
Flexural Strength	195 MPa	28300 psi	ISO 178
	200 MPa	29000 psi	ASTM D790
Flexural Modulus	17.2 GPa	2490 ksi	ASTM D790
	18.0 GPa	2610 ksi	ISO 178
Compressive Strength	285 MPa	41300 psi	ASTM D695
Poissons Ratio	0.36	0.36	ASTM E132
Izod Impact, Notched	0.530 J/cm @Thickness 3.18 mm	0.993 ft-lb/in @Thickness 0.125 in	ASTM D256
Izod Impact, Unnotched	2.10 J/cm @Thickness 3.18 mm	3.93 ft-lb/in @Thickness 0.125 in	ASTM D256
Izod Impact, Notched (ISO)	6.00 kJ/mÂ²	2.86 ft-lb/inÂ²	Notch A; ISO 180
Izod Impact, Unnotched (ISO)	14.0 kJ/mÂ²	6.66 ft-lb/inÂ²	ISO 180

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	15.0 Âµm/m-Â°C @Temperature 100 - 200 Â°C	8.33 Âµin/in-Â°F @Temperature 212 - 392 Â°F	2
	15.0 Âµm/m-Â°C @Temperature -50.0 - 50.0 Â°C	8.33 Âµin/in-Â°F @Temperature -58.0 - 122 Â°F	2
CTE, linear, Transverse to Flow	30.0 Âµm/m-Â°C @Temperature -50.0 - 50.0 Â°C	16.7 Âµin/in-Â°F @Temperature -58.0 - 122 Â°F	TMA; ASTM E831
	70.0 Âµm/m-Â°C @Temperature 100 - 200 Â°C	38.9 Âµin/in-Â°F @Temperature 212 - 392 Â°F	TMA; ASTM E831
Thermal Conductivity	0.580 W/m-K	4.03 BTU-in/hr-ftÂ²-Â°F	ASTM C177
Maximum Service Temperature, Air	220 - 240 Â°C	428 - 464 Â°F	UL Temperature Rating
Deflection Temperature at 1.8 MPa (264 psi)	265 Â°C	509 Â°F	Unannealed; ASTM D648
Flammability, UL94	V-0 @Thickness 1.60 mm	V-0 @Thickness 0.0630 in
	5VA @Thickness 1.60 mm	5VA @Thickness 0.0630 in
Oxygen Index	61 %	61 %	ASTM D2863

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+15 ohm-cm	1.00e+15 ohm-cm	ASTM D257
Surface Resistance	1.00e+16 ohm	1.00e+16 ohm	ASTM D257
Insulation Resistance	1.00e+11 ohm @Temperature 90.0 Â°C	1.00e+11 ohm @Temperature 194 Â°F	IEC 60167
Dielectric Constant	4.8 @Frequency 1000 Hz	4.8 @Frequency 1000 Hz	ASTM D150
	4.9 @Frequency 1.00e+6 Hz	4.9 @Frequency 1.00e+6 Hz	ASTM D150
Dielectric Strength	18.0 kV/mm	457 kV/in	ASTM D149
Dissipation Factor	0.0020 @Frequency 1.00e+6 Hz	0.0020 @Frequency 1.00e+6 Hz	ASTM D150
	0.0040 @Frequency 1000 Hz	0.0040 @Frequency 1000 Hz	ASTM D150
Arc Resistance	185 sec	185 sec	ASTM D495
Comparative Tracking Index	250 V	250 V	UL 746

Descriptive Properties	Value	Comments
Availability	Asia Pacific
	Europe
	Latin America
	North America
Color	Black
Form	Pellets
Processing Technique	Injection Molding
RoHS Compliance	RoHS Compliant