Solvay Specialty Polymers PrimoSpire® PR-351 Polyphenylene, Self-Reinforced (SRP)
| Category | Polymer , Thermoplastic |
| Manufacturer | Solvay Specialty Polymers |
| Trade Name | PrimoSpire® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Specialty Polymers PrimoSpire® PR-351 Polyphenylene, Self-Reinforced (SRP).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PrimoSpire® PR-351 resin is a higher flow, injection molding grade of PrimoSpire® self-reinforced polyphenylene (SRP). PrimoSpire® SRP resin is an ultra-high performance amorphous, melt-processable thermoplastic. The unique properties of this material are due primarily to the rigid-rod chemical structure. PrimoSpire® SRP is differentiated from other thermoplastics by outstanding mechanical properties without fiber reinforcement. In addition, it offers scratch resistance, great friction and wear properties, excellent solvent resistance and exceptional low temperature performance.Features: Balanced Stiffness/Toughness; Ductile; Flame Retardant; Good Chemical Resistance; Low Temperature ResistantUses: Aircraft Applications; Electrical/Electronic Applications; Industrial Applications; Medical/Healthcare ApplicationsAdditional Properties: Dynatup - ASTM D3763 58.0 JInformation provided by Solvay Specialty Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in³ | ASTM D792 |
| Melt Flow | 15 g/10 min @Load 5.00 kg, Temperature 380 °C |
15 g/10 min @Load 11.0 lb, Temperature 716 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 115 MPa | 16700 psi | ASTM D638 |
| Elongation at Break | 15 % | 15 % | 5 mm/min; ASTM D638 |
| Tensile Modulus | 3.90 GPa | 566 ksi | ASTM D638 |
| Flexural Strength | 164 MPa | 23800 psi | ASTM D790 |
| Flexural Modulus | 4.00 GPa | 580 ksi | ASTM D790 |
| Izod Impact, Notched | 0.690 J/cm | 1.29 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 171 °C | 340 °F | Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 365 °C | 689 °F | |
| Middle Barrel Temperature | 370 °C | 698 °F | |
| Front Barrel Temperature | 375 °C | 707 °F | |
| Nozzle Temperature | 374 °C | 705 °F | |
| Melt Temperature | 375 °C | 707 °F | |
| Mold Temperature | 135 - 160 °C | 275 - 320 °F | |
| Drying Temperature | 150 °C @Time 14400 sec |
302 °F @Time 4.00 hour |
|
| Shot Size | 30 - 70 % | 30 - 70 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| Latin America | ||
| North America | ||
| Color | Black | |
| Form | Pellets | |
| Processing Technique | Compression Molding; Film Extrusion | |
| Injection Molding; Machining; Profile Extrusion |
Users viewing this material also viewed the following:
- MarkeTech Cu/Mo/Cu 1:1:1 Laminated Sheet
- Mitsubishi Xantar® C CF 407 Polycarbonate/ABS Blend
- Spartech 2850-50 PVC for Regulated Applications
- Shin-Etsu Silicones KE-3490 Silicone, RTV
- Ascend Performance Materials Vydyne® ECO315 BK06 Nylon 66/6, Flame Retardant, DAM
- Beijing Ranger Chem PBT-201-G15 291 Flame Retarding FR PBT
- A. Schulman ComAlloy Hiloy® 630 Nylon 6/6, Glass/Mineral Reinforced, Flow Enhanced, UL
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, Hardness 50A, Non-Black Sulfur Cure
- Zhejiang Juner PA-A6-6H High CTI Value Halogen-Free Environmental Protection Flame-Resistant and Reinforced Polyamide
- SABIC Innovative Plastics NORYL FE8000S PPE+PS
Copyright © lookpolymers.com All Rights Reserved