- Solvay Specialty Polymers Lavanta® 5115 WH224 Polyester, High Performance (HPP), 15% Glass Fiber
Solvay Specialty Polymers Lavanta® 5115 WH224 Polyester, High Performance (HPP), 15% Glass Fiber
| Category | Polymer , Thermoplastic , Polyester, TP |
| Manufacturer | Solvay Specialty Polymers |
| Trade Name | Lavanta® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Specialty Polymers Lavanta® 5115 WH224 Polyester, High Performance (HPP), 15% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Lavanta® 5115 WH224 is a 15% glass fiber reinforced, high-performance polyester (HPP) injection molding grade developed specifically for HB LED packaging applications that utilize surface mount technology. Lavanta® 5115 WH224 has high reflectivity with excellent whiteness retention even after thermal and light aging. This gives it excellent reliability for LEDs that operate at high junction temperatures.Features: Fast Molding Cycle; Good Chemical Resistance; Good Color Stability; High Reflectivity; High Stiffness; Light Stabilized; Low Moisture AbsorptionUses: LEDsAdditional Properties: Optical Reflectivity - ASTM E1331 > 95 %; Optical Reflectivity - ASTM E1331 > 95 %; Optical Reflectivity - ASTM E1331 > 96 %Information provided by Solvay Specialty Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.62 g/cc | 0.0585 lb/in³ | ASTM D792 |
| Filler Content | 15 % | 15 % | Glass Fiber |
| Water Absorption | 0.048 % @Time 86400 sec |
0.048 % @Time 24.0 hour |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0039 cm/cm | 0.0039 in/in | |
| Linear Mold Shrinkage, Transverse | 0.012 cm/cm | 0.012 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 73.3 MPa | 10600 psi | ISO 527-2 |
| Elongation at Break | 1.5 % | 1.5 % | ISO 527-2 |
| Tensile Modulus | 6.73 GPa | 976 ksi | ISO 527-2 |
| Flexural Strength | 108 MPa | 15700 psi | ISO 178 |
| Flexural Modulus | 6.23 GPa | 904 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 2.40 kJ/m² | 1.14 ft-lb/in² | Type 1, Notch A; ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C @Temperature 200 - 250 °C |
11.1 µin/in-°F @Temperature 392 - 482 °F |
3 |
| 29.0 µm/m-°C @Temperature 50.0 - 100 °C |
16.1 µin/in-°F @Temperature 122 - 212 °F |
3 | |
| 170 µm/m-°C @Temperature 150 - 200 °C |
94.4 µin/in-°F @Temperature 302 - 392 °F |
3 | |
| CTE, linear, Transverse to Flow | 58.0 µm/m-°C @Temperature 50.0 - 100 °C |
32.2 µin/in-°F @Temperature 122 - 212 °F |
TMA; ASTM E831 |
| 100 µm/m-°C @Temperature 100 - 150 °C |
55.6 µin/in-°F @Temperature 212 - 302 °F |
TMA; ASTM E831 | |
| 120 µm/m-°C @Temperature 150 - 200 °C |
66.7 µin/in-°F @Temperature 302 - 392 °F |
TMA; ASTM E831 | |
| 140 µm/m-°C @Temperature 200 - 250 °C |
77.8 µin/in-°F @Temperature 392 - 482 °F |
TMA; ASTM E831 | |
| Melting Point | 289 °C | 552 °F | ISO 11357-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 269 °C | 516 °F | HDT B; Unannealed; ISO 75-2/B |
| Deflection Temperature at 1.8 MPa (264 psi) | 214 °C | 417 °F | Unannealed; ISO 75-2/A |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 305 °C | 581 °F | |
| Front Barrel Temperature | 290 °C | 554 °F | |
| Melt Temperature | 295 - 310 °C | 563 - 590 °F | |
| Mold Temperature | 130 - 150 °C | 266 - 302 °F | |
| Drying Temperature | 120 °C @Time 14400 sec |
248 °F @Time 4.00 hour |
|
| Moisture Content | <= 0.030 % | <= 0.030 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| Latin America | ||
| North America | ||
| Color | White | |
| Form | Pellets | |
| Processing Technique | Injection Molding |
Users viewing this material also viewed the following:
- Asahi Kasei Tenac® LA531 Acetal Homopolymer, High Lubricity (discontinued **)
- SABIC Innovative Plastics NORYL WCD861A PPE-TPE (Asia Pacific)
- Spartech Spectar® Copolyester Sheet
- SABIC Innovative Plastics LNP STAT-KON RFD03 PA 66 (Asia Pacific)
- Saint-Gobain Tygon® E-1000 Ultra-Soft Laboratory Tubing
- Chase Plastics CP Pryme® N300HSL (COND, 50% RH) Nylon 6 (Utility Grade), Heat Stabilized, Internally Lubricated
- Bostik 2107 General Purpose EVA Glue Stick
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 20 PHR N650 Filler
- Styrolution Luran® S KR 2863 C UV Colored ASA+PC
- Ascend Performance Materials Vydyne® 75HF Nylon 66/6, Heat Stabilized, Conditioned
Copyright © lookpolymers.com All Rights Reserved