Solvay Specialty Polymers Halar® 902 Polyethylene, Chlorotrifluoroethylene (ECTFE)  (Unverified Data**)<

Category Polymer , Thermoplastic , Fluoropolymer , ETFE/ECTFE , ECTFE Fluoropolymer
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Halar® 902 Polyethylene, Chlorotrifluoroethylene (ECTFE)  (Unverified Data**)<.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Specific Gravity 1.68 g/cc
1.68 g/cc
ASTM D792
Water Absorption at Saturation <= 0.10 %
<= 0.10 %
ASTM D570
Linear Mold Shrinkage, Flow 0.025 cm/cm
0.025 in/in
ASTM D955
Melt Flow 1.0 g/10 min

@Load 2.16 kg,
Temperature 275 °C
 1.0 g/10 min

@Load 4.76 lb,
Temperature 527 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 90
90
R-Scale; ASTM D785
Hardness, Shore D 75
75
ASTM D2240
Tensile Strength at Break 47.0 MPa

@Temperature 23.0 °C
 6820 psi

@Temperature 73.4 °F
 50 mm/min; ASTM D638
Tensile Strength, Yield 30.0 MPa

@Temperature 23.0 °C
 4350 psi

@Temperature 73.4 °F
 50 mm/min; ASTM D638
Elongation at Break 250 %

@Temperature 23.0 °C
 250 %

@Temperature 73.4 °F
 50 mm/min; ASTM D638
Elongation at Yield 5.0 %

@Temperature 23.0 °C
 5.0 %

@Temperature 73.4 °F
 50 mm/min; ASTM D638
Tensile Modulus 1.66 GPa

@Temperature 23.0 °C
 241 ksi

@Temperature 73.4 °F
 50 mm/min; ASTM D638
Flexural Strength 47.0 MPa

@Temperature 23.0 °C
 6820 psi

@Temperature 73.4 °F
 2.5 mm/min; ASTM D790
Flexural Modulus 1.69 GPa

@Temperature 23.0 °C
 245 ksi

@Temperature 73.4 °F
 2.5 mm/min; ASTM D790
Izod Impact, Notched 2.10 J/cm

@Thickness 3.20 mm,
Temperature -40.0 °C
 3.93 ft-lb/in

@Thickness 0.126 in,
Temperature -40.0 °F
 ASTM D256
NB

@Thickness 3.20 mm,
Temperature 23.0 °C
 NB

@Thickness 0.126 in,
Temperature 73.4 °F
 ASTM D256
Coefficient of Friction, Dynamic 0.20
0.20
vs. Itself; ASTM D1894
Coefficient of Friction, Static 0.20
0.20
vs. Itself; ASTM D1894
Taber Abrasion, mg/1000 Cycles 5.0

@Load 0.500 kg
 5.0

@Load 1.10 lb
 CS-17 Wheel
Thermal Properties Metric English Comments
Heat of Fusion 28.0 J/g
12.0 BTU/lb
Crystallization Heat; ASTM D3418
28.0 J/g
12.0 BTU/lb
ASTM D3418
CTE, linear, Parallel to Flow 100 µm/m-°C
55.6 µin/in-°F
ASTM D696
Specific Heat Capacity 0.962 J/g-°C

@Temperature 23.0 °C
 0.230 BTU/lb-°F

@Temperature 73.4 °F
 ASTM D3418
Thermal Conductivity 0.150 W/m-K

@Temperature 40.0 °C
 1.04 BTU-in/hr-ft²-°F

@Temperature 104 °F
 ASTM C177
Melting Point 225 °C
437 °F
ASTM D3418
Crystallization Temperature 205 °C
401 °F
Peak, DSC; ASTM D3418
Deflection Temperature at 0.46 MPa (66 psi) 90.0 °C
194 °F
Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 65.0 °C
149 °F
Unannealed; ASTM D648
Brittleness Temperature <= -76.0 °C
<= -105 °F
ASTM D746A
Glass Transition Temp, Tg 85.0 °C
185 °F
DMA
Decomposition Temperature 405 °C
761 °F
1% mass loss, N2; TGA
Flammability, UL94 V-0
V-0
UL 94
Oxygen Index 52 %
52 %
ASTM D2863
Electrical Properties Metric English Comments
Volume Resistivity 5.50e+16 ohm-cm

@Temperature 23.0 °C
 5.50e+16 ohm-cm

@Temperature 73.4 °F
 50% RH; ASTM D257
Dielectric Constant 2.57

@Frequency 1.00e+6 Hz,
Temperature 23.0 °C
 2.57

@Frequency 1.00e+6 Hz,
Temperature 73.4 °F
 ASTM D150
Dielectric Strength 14.0 kV/mm

@Thickness 3.20 mm,
Temperature 23.0 °C
 356 kV/in

@Thickness 0.126 in,
Temperature 73.4 °F
 ASTM D149
Descriptive Properties Value Comments
Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
Features High Viscosity
Forms Pellets
Powder
Generic ECTFE
Processing Method Extrusion
Users viewing this material also viewed the following: