- Solvay Specialty Polymers Halar® 1400LC Ethylene Chlorotrifluoroethylene Copolymer (ECTFE)
Solvay Specialty Polymers Halar® 1400LC Ethylene Chlorotrifluoroethylene Copolymer (ECTFE)
| Category | Polymer , Thermoplastic , Fluoropolymer , ETFE/ECTFE , ECTFE Fluoropolymer |
| Manufacturer | Solvay Specialty Polymers |
| Trade Name | Halar® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Specialty Polymers Halar® 1400LC Ethylene Chlorotrifluoroethylene Copolymer (ECTFE).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Low ViscosityUses: FibersAdditional Properties: Crystallization Heat - ASTM D3418 40.0 J/g; Heat of Fusion - ASTM D3418 42.0 J/g; Thermal Stability - TGA 300 °CInformation provided by Solvay Specialty Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.68 g/cc | 0.0607 lb/in³ | ASTM D792 |
| Water Absorption at Saturation | <= 0.10 % | <= 0.10 % | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.025 cm/cm | 0.025 in/in | |
| Melt Flow | 430 - 550 g/10 min @Load 2.16 kg, Temperature 275 °C |
430 - 550 g/10 min @Load 4.76 lb, Temperature 527 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 73 | 73 | ASTM D785 |
| Hardness, Shore D | 69 | 69 | ASTM D2240 |
| Tensile Strength at Break | 19.0 - 29.0 MPa | 2760 - 4210 psi | 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 30.0 MPa | 4350 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 1.0 - 10 % | 1.0 - 10 % | 50 mm/min; ASTM D638 |
| Elongation at Yield | 1.0 - 10 % | 1.0 - 10 % | 50 mm/min; ASTM D638 |
| Tensile Modulus | 1.78 GPa | 258 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 45.0 - 47.0 MPa | 6530 - 6820 psi | 2.5 mm/min; ASTM D790 |
| Flexural Modulus | 1.69 GPa | 245 ksi | 2.5 mm/min; ASTM D790 |
| Izod Impact, Notched | 0.190 J/cm @Thickness 3.20 mm, Temperature -40.0 °C |
0.356 ft-lb/in @Thickness 0.126 in, Temperature -40.0 °F |
ASTM D256 |
| 0.250 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
0.468 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 | |
| Coefficient of Friction, Dynamic | 0.20 | 0.20 | vs. Itself; ASTM D1894 |
| Coefficient of Friction, Static | 0.30 | 0.30 | vs. Itself; ASTM D1894 |
| Taber Abrasion, mg/1000 Cycles | 5.0 | 5.0 | CS-17 Wheel, 500 g; ASTM D1044 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 100 µm/m-°C | 55.6 µin/in-°F | |
| Specific Heat Capacity | 0.962 J/g-°C | 0.230 BTU/lb-°F | ASTM C351 |
| Thermal Conductivity | 0.150 W/m-K @Temperature 40.0 °C |
1.04 BTU-in/hr-ft²-°F @Temperature 104 °F |
ASTM C177 |
| Melting Point | 242 °C | 468 °F | DSC |
| Crystallization Temperature | 222 °C | 432 °F | Peak; ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 109 °C | 228 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 68.0 °C | 154 °F | Unannealed; ASTM D648 |
| Brittleness Temperature | 20.0 °C | 68.0 °F | Procedure A; ASTM D746 |
| Glass Transition Temp, Tg | 85.0 °C | 185 °F | ASTM E1356 |
| Flammability, UL94 | V-0 | V-0 | |
| Oxygen Index | 52 % | 52 % | ASTM D2863 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 5.50e+16 ohm-cm | 5.50e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 2.57 @Frequency 1.00e+6 Hz |
2.57 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Dielectric Strength | 14.0 kV/mm @Thickness 3.18 mm |
356 kV/in @Thickness 0.125 in |
ASTM D149 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| Latin America | ||
| North America | ||
| Form | Pellets | |
| Processing Technique | Extrusion |
Users viewing this material also viewed the following:
- Gouda Vuurvast CURON 150 RN Dense Refractory Castable
- Haynes 625 alloy, plate after 8000 hours at 650°C (1200°F)
- Eagle Brass 510 Phosphor Bronzes 5% A, Hard
- DSM Akulon® K224-HG7 Nylon 6-35% Glass Reinforced (European Grade) (Cond)
- Domo 2600M Polypropylene Copolymer
- DuPont Performance Polymers Hytrel® G4078LS NC010 Polyester Elastomer TPC-ET (Unverified Data**)
- Arkema Group Rilsan® AMN D Nylon 12, Rigid, Injection Grade (Dry)
- Braskem TI71200M High Crystallinity Copolymer Polypropylene
- BASF Ultramid® 8253 HS BK-102 PA6 (Dry)
- Victrex® PEEK 450G903 Black Polyetheretherketone, Unreinforced
Copyright © lookpolymers.com All Rights Reserved