Solvay Specialty Polymers Amodel® HFZ A-1145 L Polyphthalamide (PPA) (Unverified Data**)

Category	Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 50% Glass Fiber Reinforced
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Solvay Specialty Polymers Amodel® HFZ A-1145 L Polyphthalamide (PPA) (Unverified Data**).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Amodel® HFZ A-1145 L is a high-flow, 45% glass-fiber-reinforced grade. - Natural: HFZ A-1145 L NT - Black: HFZ A-1145 L BK 937Information provided by Solvay Specialty Polymers.

Physical Properties	Metric	English	Comments
Density	1.61 g/cc	0.0582 lb/in³	ISO 1183/A
Filler Content	45 %	45 %	Glass Fiber Reinforcement

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	232 MPa	33600 psi	ISO 527-2
Elongation at Break	1.8 % @Temperature 23.0 °C	1.8 % @Temperature 73.4 °F	ISO 527-2
Tensile Modulus	15.1 GPa	2190 ksi	ISO 527-2
Flexural Strength	330 MPa	47900 psi	ISO 178
Flexural Modulus	14.0 GPa @Temperature 23.0 °C	2030 ksi @Temperature 73.4 °F	ISO 178
Izod Impact, Notched (ISO)	7.80 kJ/m²	3.71 ft-lb/in²	ISO 180
Charpy Impact, Notched	0.990 J/cm²	4.71 ft-lb/in²	ISO 179

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	302 °C	576 °F	Unannealed; ISO 75-2/Af

Processing Properties	Metric	English
Rear Barrel Temperature	316 - 329 °C	601 - 624 °F
Middle Barrel Temperature	316 - 329 °C	601 - 624 °F
Front Barrel Temperature	324 - 335 °C	615 - 635 °F
Melt Temperature	321 - 343 °C	610 - 649 °F
Mold Temperature	150 °C	302 °F
Drying Temperature	120 °C	248 °F
Dry Time	4.00 hour	4.00 hour
Moisture Content	0.030 - 0.060 %	0.030 - 0.060 %

Descriptive Properties	Value	Comments
Appearance	Black
	Natural Color
Availability	Africa & Middle East
	Asia Pacific
	Europe
	North America
	South America
Features	Good Chemical Resistance
	Good Creep Resistance
	Good Dimensional Stability
	Good Stiffness
	High Flow
	High Stiffness
	High Strength
	High Temperature Strength
	Low Moisture Absorption
Forms	Pellets
Generic	PPA
Processing Method	Injection Molding
Uses	Automotive Applications
	Automotive Electronics
	Automotive Under the Hood
	Bobbins
	Connectors
	Electrical/Electronic Applications
	General Purpose
	Industrial Applications
	Industrial Parts
	Lawn and Garden Equipment
	Machine/Mechanical Parts
	Metal Replacement