| Category | Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 20% Glass Fiber Reinforced |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Specialty Polymers Amodel® A-1115 HS Polyphthalamide (PPA) Resin, 15% Glass Reinforced, at 50% RH
(dis.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
AMODEL A-1115 HS resin is a 15% glass reinforced, heat stabilized polyphthalamide (PPA) which exhibits a high deflection temperature, high flexural modulus, and high tensile strength. Excellent creep resistance and low moisture absorption are also characteristic of this resin. AMODEL A-1115 HS resin can be easily processed using conventional equipment and methods.This product line was acquired by Solvay Advanced Polymers from BP Amoco in November 2001.MatWeb has an entry for this material dry as molded.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.26 g/cc | 0.0455 lb/in³ | Dry As Molded |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 112 MPa | 16200 psi | ASTM D638 |
| Elongation at Break | 1.9 % | 1.9 % | ASTM D638 |
| Tensile Modulus | 8.30 GPa | 1200 ksi | ASTM D638 |
| Flexural Yield Strength | 161 MPa | 23400 psi | ASTM D790 |
| Flexural Modulus | 6.20 GPa | 899 ksi | ASTM D790 |
| Compressive Yield Strength | 190 MPa | 27600 psi | ASTM D695 |
| Shear Strength | 81.0 MPa | 11700 psi | ASTM D732 |
| Izod Impact, Notched | 0.360 J/cm | 0.674 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 2.00e+15 ohm-cm | 2.00e+15 ohm-cm | ASTM D257 |
| Dielectric Constant | 4.0 @Frequency 1e+6 Hz |
4.0 @Frequency 1e+6 Hz |
ASTM D150 |
| 4.4 @Frequency 60 Hz |
4.4 @Frequency 60 Hz |
ASTM D150 | |
| Dielectric Strength | 19.0 kV/mm | 483 kV/in | ASTM D149 |
| Dissipation Factor | 0.0080 @Frequency 60 Hz |
0.0080 @Frequency 60 Hz |
ASTM D150 |
| 0.023 @Frequency 1e+6 Hz |
0.023 @Frequency 1e+6 Hz |
ASTM D150 | |
| Arc Resistance | 115 sec | 115 sec | ASTM D495 |
| Comparative Tracking Index | 550 V | 550 V |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 321 - 343 °C | 610 - 649 °F | Injection |
Users viewing this material also viewed the following:
- LATI LARIL 13 G/10 10% Glass Fiber Reinforced Polyphenylene Oxide (PPOm) (discontinued **)
- Carmel Olefins IPETHENE® 800 Low Density Polyethylene (discontinued **)
- Haysite 43000 Polyester SMC, 22% Glass Reinforced
- LATI Latigloss 57 G/50 F2 PPA, 50% Glass Fiber Reinforced
- Azoty Tarnow™ TARNOFORM 500 GB6 POM
- Multibase Multi-Flex® TPE A 7606 UV NAT
- Solvay Specialty Polymers Torlon® 7130 Polyamide-imide (PAI) (Unverified Data**)
- PolyOne Stat-Tech™ RA-06CF-09GF/000 EM Polyarylsulfone - ESD Applications - Flow Enhanced Grade (discontinued
- PolyOne Edgetek® AM 33 GF/000 L HS Black Polyphthalamide (PPA), Glass Filled (discontinued **)
- Ineos ABS Triax® KU2-3154 ABS + Polyamide Blend (DAM), Injection Molding Grade
Copyright © lookpolymers.com All Rights Reserved