Solvay Engineered Polymers DEXFLEX® 930HS TPO (discontinued **)

Category	Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Olefinic Elastomer (TPO) , Polyolefin
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Solvay Engineered Polymers DEXFLEX® 930HS TPO (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: DEXFLEX® 930HS is a thermoplastic olefinic elastomer (TPO) designed for large automotive exterior applications that require high flow for excellent processability, ductile impact properties at low temperatures, and good paint adhesion. Applications Bumper fascias Information provided by Solvay Engineered PolymersLyondellBasell acquired Solvay Engineered Polymers in 2008. This grade is not part of the current LyondellBasell product line.

Physical Properties	Metric	English	Comments
Specific Gravity	0.910 g/cc	0.910 g/cc	ISO 1183
Linear Mold Shrinkage	0.010 - 0.013 cm/cm	0.010 - 0.013 in/in	as molded; ISO 294
	0.014 - 0.017 cm/cm	0.014 - 0.017 in/in	after bake; ISO 294
Melt Flow	21 g/10 min	21 g/10 min	ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	17.0 MPa	2470 psi	150x10x4 mm specimen, 50 mm/min; ISO 527-1/527-2
Flexural Modulus	0.910 GPa	132 ksi	80x10x4 mm specimen, 2 mm/min; ISO 178
Impact Test	18.0 J	13.3 ft-lb	multiaxial, 2.2 m/s; ASTM D3763

Thermal Properties	Metric	English	Comments
CTE, linear	75.0 µm/m-°C @Temperature -30.0 - 80.0 °C	41.7 µin/in-°F @Temperature -22.0 - 176 °F	ASTM E228