Silon Taborex TA 1135 HD Chemically-Crosslinkable HDPE Compound
| Category | Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Crosslinkable |
| Manufacturer | Silon |
| Trade Name | Taborex |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Silon Taborex TA 1135 HD Chemically-Crosslinkable HDPE Compound.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
TABOREX TA 1135 HD is a crosslinkable compound made by Silane grafted ethylene polymer. This graft polymer constitutes together with a Masterbatch containing the crosslinking catalyst a “SIOPLAS-SYSTEMâ€. It is used for the production of multi-layer pipes for domestic hot and cold water, under floor heating and central heating application. It is designed to achieve best performance in single layer and co-extrusion products.Information provided by Silon
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.560 g/cc | 0.0202 lb/in³ | DIN 53466 |
| Density | 0.949 g/cc | 0.0343 lb/in³ | DIN 53479/ASTM D1505 |
| Volatiles | <= 0.10 % | <= 0.10 % | ITM-ZP 300CH 3-5-5/d |
| Melt Flow | 0.60 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.60 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133/ASTM D1238 |
| 3.5 g/10 min @Load 5.00 kg, Temperature 190 °C |
3.5 g/10 min @Load 11.0 lb, Temperature 374 °F |
ISO 1133/ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 25.0 MPa | 3630 psi | ISO R 527 |
| Elongation at Break | 250 % | 250 % | ISO R 527 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 160 - 170 °C | 320 - 338 °F | |
| Zone 2 | 170 - 180 °C | 338 - 356 °F | |
| Zone 3 | 170 - 190 °C | 338 - 374 °F | |
| Zone 4 | 170 - 190 °C | 338 - 374 °F | |
| Die Temperature | 190 - 220 °C | 374 - 428 °F | |
| Head Temperature | 200 - 210 °C | 392 - 410 °F | |
| Screw Cooling Temperature | 70.0 - 90.0 °C | 158 - 194 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Gel content (%) | 70 | EN 579 |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 6 NG GF 45 SGF PA6, improved strength, light stability
- SABIC Innovative Plastics Lexan® HFD1232 PC Copolymer
- ExxonMobil Optema® TC-221 Ethylene Methyl Acrylate for Compounding (discontinued **)
- DuPont 20 Series 2020 Specialty Polyethylene Resin (discontinued **)
- Solvay Specialty Polymers Solef® 3208/0150 Anti-friction PVDF Compound (discontinued **)
- Gwent Electronic Materials C2050905D3 80:20 Silver Palladium Ink
- Styron Sprintan® SLR 4601 Solution Styrene Butadiene Rubber (S-SBR)
- Ashley Polymers Ashlene® 735LD Nylon 6
- Ashley Polymers Ashlene® D925 Nylon 12
Copyright © lookpolymers.com All Rights Reserved