ExxonMobil Escorene® LD-411 LDPE Power Cable Insulation (discontinued **)

Category	Polymer , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Wire/Cable Grade
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil Escorene® LD-411 LDPE Power Cable Insulation (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Data provided by the manufacturer, Exxon Chemical.A crosslinkable polyethylene homopolymer designed as an electrical grade base resin especially suitable for Henschel blending.Applications: A base resin for fully formulated crosslinkable medium voltage cable insulation compounds.

Physical Properties	Metric	English	Comments
Density	0.921 g/cc	0.0333 lb/in³	Exxon Method
Environmental Stress Crack Resistance	<= 1.0 hour	<= 1.0 hour	F50, Condition A; ASTM D-1693
Melt Flow	2.3 g/10 min	2.3 g/10 min	Exxon Method

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	45	45	ASTM D2240
Tensile Strength, Ultimate	10.3 MPa	1490 psi	ASTM D638
Elongation at Break	600 %	600 %	ASTM D638
Flexural Modulus	0.200 GPa	29.0 ksi	ASTM D790

Thermal Properties	Metric	English	Comments
Melting Point	109 °C	228 °F	Exxon Method
Brittleness Temperature	<= -72.0 °C	<= -97.6 °F	ASTM D746

Electrical Properties	Metric	English	Comments
Dielectric Constant	2.26 @Frequency 1e+6 Hz	2.26 @Frequency 1e+6 Hz	ASTM D150
Dielectric Strength	21.0 kV/mm @Thickness 3.17 mm	533 kV/in @Thickness 0.125 in	ASTM D149
Dissipation Factor	0.00010 @Frequency 1e+6 Hz	0.00010 @Frequency 1e+6 Hz	ASTM D150