- Sichuan Deyang Haton® hGR515 Polyphenylene Sulfide/PA Alloy
Sichuan Deyang Haton® hGR515 Polyphenylene Sulfide/PA Alloy
| Category | Polymer , Thermoplastic , Nylon , Polyphenylene Sulfide (PPS) |
| Manufacturer | Sichuan Deyang Chemical Co. Ltd. |
| Trade Name | Haton® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sichuan Deyang Haton® hGR515 Polyphenylene Sulfide/PA Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Injection molding, high strengthInformation provided by Sichuan Deyang Chemical Co., LTD
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.70 g/cc | 0.0614 lb/in³ | GB/T 1033.1-2008 |
| Water Absorption | 0.020 % | 0.020 % | GB/T 1034-2008 |
| Linear Mold Shrinkage, Flow | 0.0033 cm/cm | 0.0033 in/in | GB/T 15585-1995 |
| Linear Mold Shrinkage, Transverse | 0.0033 cm/cm | 0.0033 in/in | GB/T 15585-1995 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell L | 110 | 110 | GB/T 3398.2-2008 |
| Tensile Strength | 220 MPa | 31900 psi | GB/T 1040.2-2006 |
| Elongation at Break | 1.4 % | 1.4 % | GB/T1040.2-2006 |
| Flexural Strength | 330 MPa | 47900 psi | GB/T 9341-2008 |
| Flexural Modulus | 18.6 GPa | 2700 ksi | GB/T 9341-2008 |
| Izod Impact, Notched (ISO) | 14.2 kJ/m² | 6.76 ft-lb/in² | GB/T 1843-2008 |
| Izod Impact, Unnotched (ISO) | 66.0 kJ/m² | 31.4 ft-lb/in² | GB/T 1843-2008 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 280 °C | 536 °F | GBT/T 19466.3-2004 |
| Deflection Temperature at 1.8 MPa (264 psi) | 255 °C | 491 °F | GB/T 1634.2-2004 |
| Flammability, UL94 | V-2 | V-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.60e+16 ohm-cm | 1.60e+16 ohm-cm | GB/T1410-2006 |
| Surface Resistivity per Square | 2.00e+15 ohm | 2.00e+15 ohm | GB/T1410-2006 |
| Dielectric Constant | 4.0 | 4.0 | GB/T 1409-2006 |
| Dielectric Strength | 16.0 kV/mm | 406 kV/in | GB/T1408.1-2006 |
| Dissipation Factor | 0.0020 | 0.0020 | GB/T 1409-2006 |
Users viewing this material also viewed the following:
- Ritelok PR1500 Plastic & Rubber Adhesive
- SABIC Innovative Plastics Lexan® 143R PC (Europe-Africa-Middle East)
- Chevron Phillips mPact™ D352 m-LLDPE Linear Low Density Polyethylene (discontinued **)
- Lehmann & Voss LUVOCOM® 19-8373 Polyamide 46, with carbon fiber, lubricant modified
- Kolon KOCETAL® K300LO Low Odor Acetal Resin
- Total Xsene® XS10 OS HDPE, pipe
- Chem Polymer Chemlon 275 Nylon 6, Copolymer Impact Modified
- Dow Corning 3120 RTV SILICONE RUBBER
- Trelleborg Horda Cable E8465 Easy Strippable Semiconductive Shielding
- Arkema Group KYNAR FLEX® 2850-07 Polyvinylidene Fluoride Copolymer - Extrusion & Molding
Copyright © lookpolymers.com All Rights Reserved