Schwartz Technical Plastics LAMINEX® 2040 Cotton Fabric, Phenolic Resin Impregnated, MoS2 Filled

Category Polymer , Thermoset , Phenolic , Phenolic, Novolac, Fabric Filled
Manufacturer Schwartz Technical Plastics
Trade Name LAMINEX®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Schwartz Technical Plastics LAMINEX® 2040 Cotton Fabric, Phenolic Resin Impregnated, MoS2 Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Application: slippers, gear-rods, bushesInformation provided by Schwartz Technical Plastics GmbH
Physical Properties Metric English Comments
Density 1.35 g/cc
0.0488 lb/in³
ISO R 1183
Mechanical Properties Metric English Comments
Ball Indentation Hardness 170 MPa
24700 psi
Hc 30; ISO 2039; partially
Tensile Strength, Yield 50.0 MPa
7250 psi
ISO-DIS 527
Tensile Modulus 7.00 GPa
1020 ksi
DIN 53457
Flexural Strength 80.0 - 100 MPa
11600 - 14500 psi
DIN 54352
Compressive Strength 170 MPa
24700 psi
ISO 604
Izod Impact, Notched (ISO) 15.0 kJ/m²
7.14 ft-lb/in²
DIN 53453
Izod Impact Resistance 1.80 J/cm²
8.57 ft-lb/in²
swinging hammer 0,1 DIN 51222; DIN 53453
Coefficient of Friction 0.020
0.020
With lubrication
Coefficient of Friction, Dynamic 0.020
0.020
no lube; Steel 2162, Rvst=2E-6m, p=0.05 Mpa, v=0.6 m/s, t=40°C
Thermal Properties Metric English Comments
CTE, linear 30.0 µm/m-°C

@Temperature 20.0 - 100 °C
16.7 µin/in-°F

@Temperature 68.0 - 212 °F
DIN 53752
Thermal Conductivity 0.290 W/m-K
2.01 BTU-in/hr-ft²-°F
DIN 52612
Maximum Service Temperature, Air 120 °C
248 °F
Continuous
150 °C
302 °F
Intermittent
Electrical Properties Metric English Comments
Surface Resistance 1.00e+8 ohm
1.00e+8 ohm
DIN 53482
Dielectric Constant 5.0
5.0
DIN 53483
Dielectric Loss Index 0.30
0.30
DIN 53483
Descriptive Properties Value Comments
Creepage/leakage Resistance KA1
DIN 53480
Moisture Absorption at Equilibrium 100 mg
DIN 53472