- Schwartz Technical Plastics LAMIGAMID® 700 Ultra High Molecular Weight Polyethylene
Schwartz Technical Plastics LAMIGAMID® 700 Ultra High Molecular Weight Polyethylene
| Category | Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), UHMW PE Ultra High Molecular Weight |
| Manufacturer | Schwartz Technical Plastics |
| Trade Name | LAMIGAMID® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Schwartz Technical Plastics LAMIGAMID® 700 Ultra High Molecular Weight Polyethylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Application: wear liners, sliding platesInformation provided by Schwartz Technical Plastics GmbH
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.950 g/cc | 0.0343 lb/in³ | ISO R 1183 |
| Moisture Absorption at Equilibrium | 0.00 % | 0.00 % | DIN 53473 |
| Water Absorption at Saturation | >= 0.10 % @Temperature 20.0 °C |
>= 0.10 % @Temperature 68.0 °F |
ISO R 62 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 57.0 MPa | 8270 psi | Hc 30; ISO 2039; partially |
| Tensile Strength, Yield | 39.0 MPa | 5660 psi | ISO-DIS 527 |
| Creep Strength | 3.20 MPa | 464 psi | 1% elongation, 1000 h; DIN 53444 |
| 5.00 MPa | 725 psi | 2% elongation, 1000 h; DIN 53444 | |
| Tensile Modulus | 1.10 GPa | 160 ksi | DIN 53457 |
| Flexural Strength | 40.0 MPa | 5800 psi | DIN 54352 |
| Flexural Modulus | 0.790 GPa | 115 ksi | DIN 53457 |
| Compressive Strength | 16.0 MPa | 2320 psi | 5% pressing; EN ISO 604 |
| 25.0 MPa | 3630 psi | 10% pressing; EN ISO 604 | |
| 32.0 MPa | 4640 psi | 20% pressing; EN ISO 604 | |
| Izod Impact, Notched (ISO) | NB | NB | DIN 53453 |
| Izod Impact Resistance | NB | NB | swinging hammer 0,1 DIN 51222; DIN 53453 |
| Coefficient of Friction | 0.020 - 0.080 | 0.020 - 0.080 | With lubrication |
| Coefficient of Friction, Dynamic | 0.29 | 0.29 | no lube; Steel 2162, Rvst=2E-6m, p=0.05 Mpa, v=0.6 m/s, t=40°C |
| Tear Strength Test | 4.5 | 4.5 | ISO-DIS 527 |
| K Factor (Wear Factor) | 1.0e-9 | 1.0e-9 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 200 µm/m-°C @Temperature 20.0 - 100 °C |
111 µin/in-°F @Temperature 68.0 - 212 °F |
DIN 53752 |
| Specific Heat Capacity | 2.30 J/g-°C | 0.550 BTU/lb-°F | |
| Thermal Conductivity | 0.330 W/m-K | 2.29 BTU-in/hr-ft²-°F | DIN 52612 |
| Melting Point | 136 °C | 277 °F | ISO R 1218 |
| Maximum Service Temperature, Air | 80.0 °C | 176 °F | Continuous |
| 120 °C | 248 °F | Intermittent | |
| Minimum Service Temperature, Air | -100 °C | -148 °F | Continuous |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+17 ohm-cm | 1.00e+17 ohm-cm | DIN 53482 |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | DIN 53482 |
| Dielectric Constant | 2.3 | 2.3 | DIN 53483 |
| Dielectric Strength | 100 kV/mm | 2540 kV/in | DIN 53481 |
| Dielectric Loss Index | 0.00010 | 0.00010 | DIN 53483 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Creepage/leakage Resistance | KA3c | DIN 53480 |
Users viewing this material also viewed the following:
- Nye Lubricants 723MS (RL) Rheolube Grease
- Solvay Specialty Polymers Solef® 6012 Polyvinylidene Fluoride (PVDF)
- Techmer ES HiFill® PA6 GF55 HS L 55% Glass Filled
- Silberline "A" Series A-1592FG
- Total PSI 3441 High Heat Resistance Impact Polystyrene
- ExxonMobil Santoprene® 101-45W255 Thermoplastic Elastomer
- Dow Primacor® 3150 Ethylene Acrylic Acid (EAA)
- Arlon 915-07R##-P1 0.015" (0.381 mm) Cured Self-fusing Silicone Tape
- Eastman Tenite Butyrate 465A3720010 Clear, Trsp Cellulose Acetate Butyrate (discontinued **)
Copyright © lookpolymers.com All Rights Reserved