Samyang Triel® 5720 Thermoplastics Polyetherester Elastomer, General Extrusion
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyester, TP , Polyether Ester Elastomer |
| Manufacturer | Samyang |
| Trade Name | Triel® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samyang Triel® 5720 Thermoplastics Polyetherester Elastomer, General Extrusion.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Excellent mechanical characteristics, elasticity, thermal resistance and chemical resistance.5720 is an extrusion grade.Information provided by Samyang.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.25 g/cc | 1.25 g/cc | ASTM D792 |
| Water Absorption | 0.50 % | 0.50 % | ASTM D570 |
| Linear Mold Shrinkage | 0.017 - 0.020 cm/cm | 0.017 - 0.020 in/in | ASTM D955 |
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| 2.0 g/10 min @Load 2.16 kg, Temperature 240 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 464 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 72 | 72 | ASTM D2240 |
| Tensile Strength, Ultimate | 41.7 MPa | 6040 psi | ASTM D638 |
| Tensile Strength, Yield | 24.5 MPa @Strain 5.00 % |
3560 psi @Strain 5.00 % |
ASTM D638 |
| 26.5 MPa @Strain 50.0 % |
3840 psi @Strain 50.0 % |
ASTM D638 | |
| 30.4 MPa @Strain 10.0 % |
4410 psi @Strain 10.0 % |
ASTM D638 | |
| Flexural Yield Strength | 36.3 MPa | 5260 psi | ASTM D790 |
| Flexural Modulus | 0.981 GPa | 142 ksi | ASTM D790 |
| Izod Impact, Notched | 0.490 - 0.588 J/cm @Thickness 3.17 mm, Temperature -40.0 °C |
0.918 - 1.10 ft-lb/in @Thickness 0.125 in, Temperature -40.0 °F |
ASTM D256 |
| 0.686 - 0.883 J/cm @Thickness 3.17 mm, Temperature 23.0 °C |
1.29 - 1.65 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 218 °C | 424 °F | ASTM D2117 |
| Deflection Temperature at 0.46 MPa (66 psi) | 130 °C | 266 °F | ASTM D648 |
| Vicat Softening Point | 207 °C | 405 °F | ASTM D1525 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Flexible Rate | > 400% | ASTM D638 |
Users viewing this material also viewed the following:
- Kazanorgsintez E-17 Petroleum Resin
- GEHR Plastics POM-C Acetal
- Momentive Performance Materials IS808 One-Component, Paste Consistency Silicone Rubber Adhesive Sealant, Translucent
- Lanxess Durethan® DP BM 65 X FM30 901510 Nylon 6, 65% Mineral + Glass Fiber
- Special Metals NIMONIC® Alloy 90
- A. Schulman SCHULAMID® 66 MV3HI High Impact Nylon 6/6
- Borealis Daploy™ SF203HMS High Melt Strength Polypropylene for Extrusion Coating
- DuPont Elvax® 750 Ethylene-Vinyl Acetate Copolymer Resin
- BASF Nypel® RC6030F BK 30% Glass Filled PA6 (Dry)
- Silberline Sparkle Silvet® 790-20-E
Copyright © lookpolymers.com All Rights Reserved