Samyang Triel® 5652EM Thermoplastics Polyetherester Elastomer, Extrusion
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyester, TP , Polyether Ester Elastomer |
| Manufacturer | Samyang |
| Trade Name | Triel® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samyang Triel® 5652EM Thermoplastics Polyetherester Elastomer, Extrusion.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Excellent mechanical characteristics, elasticity, thermal resistance and chemical resistance.5652EM is an extrusion grade.Information provided by Samyang.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.24 g/cc | 1.24 g/cc | ASTM D792 |
| Water Absorption | 0.50 % | 0.50 % | ASTM D570 |
| Linear Mold Shrinkage | 0.017 - 0.020 cm/cm | 0.017 - 0.020 in/in | ASTM D955 |
| Melt Flow | 10 g/10 min @Load 2.16 kg, Temperature 230 °C |
10 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 65 | 65 | ASTM D2240 |
| Tensile Strength, Ultimate | 34.3 MPa | 4980 psi | ASTM D638 |
| Flexural Yield Strength | 16.2 MPa | 2350 psi | ASTM D790 |
| Flexural Modulus | 0.358 GPa | 51.9 ksi | ASTM D790 |
| Izod Impact, Notched | 0.785 - 0.981 J/cm @Thickness 3.17 mm, Temperature -40.0 °C |
1.47 - 1.84 ft-lb/in @Thickness 0.125 in, Temperature -40.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 205 °C | 401 °F | ASTM D2117 |
| Deflection Temperature at 0.46 MPa (66 psi) | 117 °C | 243 °F | ASTM D648 |
| Vicat Softening Point | 200 °C | 392 °F | ASTM D1525 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Flexible Rate | > 400% | ASTM D638 |
Users viewing this material also viewed the following:
- Multibase Multi-Pro® 1008 T Polypropylene
- Quadrant EPP TIVAR® 1000 PE-UHMW, virgin (ISO Data)
- Polymer Resources AC-GP2 Acetal Copolymer, Medium Flow
- Resin Technology Group KONA 871 Low Cost Epoxy Resin
- Karina 801-27/13-IS-RG Smoky Clear PVC Compound
- SABIC Innovative Plastics LNP STAT-KON AE002 ABS
- Saint-Gobain Norton® Fluorglas® Chemfilm® R128/R129 Premium Grade Extruded Full Density PTFE Film (0.003" thick)
- Aclo Accucomp ABS ABS810L Medium Impact Grade
- SABIC Innovative Plastics NORYL PX2938 PPE (Asia Pacific)
Copyright © lookpolymers.com All Rights Reserved