Tra-Con Tra-Bond 216C05
| Category | Polymer , Thermoset |
| Manufacturer | Tra-Con, Inc. |
| Trade Name | Tra-Bond |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Tra-Con Tra-Bond 216C05.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Tra-Con Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.12 g/cc | 1.12 g/cc | Cured |
| Viscosity | 3000 cP | 3000 cP | Mixed (cp #40, 5 rpm) |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 62 | 62 | 24 hrs @ 25°C |
| Adhesive Bond Strength | 22.8 MPa | 3300 psi | Lap shear, alum to alum, 24 hrs @ 25°C |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 115 °C | 239 °F | |
| Minimum Service Temperature, Air | -60.0 °C | -76.0 °F | |
| Glass Transition Temp, Tg | 18.0 °C | 64.4 °F | Ultimate Tg |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Pot Life | 60.0 min @Temperature 25.0 °C |
60.0 min @Temperature 77.0 °F |
2X initial viscosity |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Amber | Cured |
Users viewing this material also viewed the following:
- Qualchem Danamid FEWL2-25 Polyamide 6, 25% Mineral Filled
- Gharda Chemicals Gafone™ T6300 Polysupersulfone (PSS) (discontinued **)
- IBC Advanced Alloys Beralcast® 310 Beryllium-Aluminum Alloy
- Special Metals Nitinol Chrome-Doped Superelastic Ni-Ti alloy
- Techmer ES Luriblend® PA6/6 CF10 TL15 BK 10% Carbon Filled
- ExxonMobil Label-Lyte™ 612LLG102 OPP Film
- Fainplast Compounds HL 88 Flexible PVC, Insulation for High Temperatures
- Arkema Group Pebax® MV 3000 SA 01 Polyether Block Amide (PEBA)
- Asahi Kasei Leona® 54G33 33% Glass Filled Nylon 66
- Plenco 50240 PET, Pellet, Injection Molded, Black (discontinued **)
Copyright © lookpolymers.com All Rights Reserved