- Samsung Cheil Industries Starex® BF-0677HF MABS, Unreinforced Scratch Resistant
Samsung Cheil Industries Starex® BF-0677HF MABS, Unreinforced Scratch Resistant
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Starex® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Starex® BF-0677HF MABS, Unreinforced Scratch Resistant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Scratch resistant material that is used in TV housing and the exterior material for cleaner and air purifierInformation provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.13 g/cc | 1.13 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm @Thickness 3.20 mm |
0.0040 in/in @Thickness 0.126 in |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0050 cm/cm @Thickness 3.20 mm |
0.0050 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 19 g/10 min @Load 10.0 kg, Temperature 220 °C |
19 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 114 | 114 | ASTM D785 |
| Tensile Strength at Break | 29.4 MPa | 4260 psi | 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 47.1 MPa | 6830 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 15 % | 15 % | 5 mm/min; ASTM D638 |
| Tensile Modulus | 2.39 GPa | 347 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 68.6 MPa | 9950 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 2.45 GPa | 356 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 0.883 J/cm @Thickness 6.35 mm |
1.65 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 1.18 J/cm @Thickness 3.17 mm |
2.20 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 93.0 °C @Thickness 6.40 mm |
199 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 84.0 °C @Thickness 6.40 mm |
183 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 96.0 °C | 205 °F | B/50; ISO R306 |
| 99.0 °C | 210 °F | B/120; ISO R306 | |
| Flammability, UL94 | HB @Thickness 1.50 - 3.00 mm |
HB @Thickness 0.0591 - 0.118 in |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Pencil Hardness | HB | 500g, JIS K 5401 |
Users viewing this material also viewed the following:
- MV Labs MN1000 MnSO4·xH2O Manganese(II) sulfate hydrate
- PolyOne OnForce™ LFT PP-40LGF/001 UV Black Polypropylene Homopolymer (PP Homopolymer)
- Pearl Engineering PEPLPET B-07C PET Bottle Grade
- Cookson Group Plaskon® 1002 Conventional Encapsulant (discontinued **)
- Borealis LE0592 Polyethylene
- ExxonMobil Coolant/Antifreeze Mobil Heavy Duty
- AK Steel SAE J1392 050 XLK, Grade 50 Aluminized Carbon Steel, High Strength Low Alloy Steel (HSLAS)
- Akro-Plastic Akromid® T6 GF30 (3501) PPA Dry, 30% Glass Filled
- Arlon 44570XB025 0.025" Uncured Silicone Rubber with Fiberglass
Copyright © lookpolymers.com All Rights Reserved