Chevron Phillips HiD® 9650 HDPE Blown Film Resin (discontinued **)

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Film Grade
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Chevron Phillips HiD® 9650 HDPE Blown Film Resin (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Resin Type: Linear Polyethylene CopolymerCharacteristics: Copolymerization Enhances Film Toughness, Excellent Film Drawdown, Unique Molecular Architecture Gives Moisture Barrier Properties Typical of Much Higher Density Resins, Excellent Heat Seal Response, Excellent Embossing Properties, Density Level Gives Excellent Machinability, Blends Well with LLDPEApplications: Notion and Millinery Bags, Multi-wall Liners, CoextrusionsFilm properties below based on film thickness of 25.4 µm.Data provided by Chevron Chemical.

Physical Properties	Metric	English	Comments
Density	0.952 g/cc	0.0344 lb/in³	ASTM D1505
Moisture Vapor Transmission	0.140 cc-mm/m²-24hr-atm	0.356 cc-mil/100 in²-24hr-atm	ASTM F1249
Melt Flow	0.34 g/10 min	0.34 g/10 min	Condition E; ASTM D 1238

Mechanical Properties	Metric	English	Comments
Film Elongation at Break, MD	460 %	460 %	ASTM D882
Film Elongation at Break, TD	650 %	650 %	ASTM D882
Secant Modulus, MD	0.710 GPa	103 ksi	ASTM D882
Secant Modulus, TD	0.830 GPa	120 ksi	ASTM D882
Elmendorf Tear Strength, MD	0.630 g/micron	16.0 g/mil	Notched; ASTM D1922
Elmendorf Tear Strength, TD	15.7 g/micron	400 g/mil	ASTM D1922
Dart Drop	3.50 g/micron	88.9 g/mil	1.5 in. dart/26 in. drop height; ASTM D 1709
Film Tensile Strength at Break, MD	51.0 MPa	7400 psi	ASTM D882
Film Tensile Strength at Break, TD	43.0 MPa	6240 psi	ASTM D882

Thermal Properties	Metric	English	Comments
Vicat Softening Point	125 °C	257 °F	ASTM D1525

Processing Properties	Metric	English	Comments
Melt Temperature	221 °C	430 °F