BASF Elastollan® 1185A10X Wire & Cable Grade Polyurethane Elastomer

Category Polymer , Thermoplastic , Elastomer, TPE , Polyurethane, TP
Manufacturer BASF
Trade Name Elastollan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Elastollan® 1185A10X Wire & Cable Grade Polyurethane Elastomer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Compliant with NSF Standard 61 (Drinking water contact). As with all TPU products this grade must be dried prior to processing.Information provided by BASF Corporation.
Physical Properties Metric English Comments
Density 1.12 g/cc

@Thickness 2.00 mm
 0.0405 lb/in³

@Thickness 0.0787 in
 molded plaque, cured 20 hr at 100°C; ASTM D792
Mechanical Properties Metric English Comments
Hardness, Shore A 86

@Thickness 2.00 mm
 86

@Thickness 0.0787 in
 molded plaque, cured 20 hr at 100°C; ASTM D2240
Tensile Strength, Ultimate 52.0 MPa

@Thickness 2.00 mm
 7540 psi

@Thickness 0.0787 in
 molded plaque, cured 20 hr at 100°C; ASTM D412
Tensile Strength, Yield 7.60 MPa

@Strain 100 %
 1100 psi

@Strain 100 %
 ASTM D-412
19.0 MPa

@Strain 300 %
 2760 psi

@Strain 300 %
 0.76 mm (0.030 in) extruded sheet; ASTM D-412
Elongation at Break 570 %
570 %
on 0.030 in extruded sheet; ASTM D-412
Flexural Modulus 0.0430 GPa

@Thickness 2.00 mm
 6.24 ksi

@Thickness 0.0787 in
 molded plaque, cured 20 hr at 100°C; ASTM D790
Tear Strength 66.0 kN/m

@Thickness 0.760 mm
 377 pli

@Thickness 0.0299 in
 Split tear strength; extruded sheet; ASTM D-1938
Graves Tear Strength 88.0 kN/m

@Thickness 0.762 mm
 502 pli

@Thickness 0.0300 in
 extruded sheet; ASTM D624
Taber Abrasion, mg/1000 Cycles 25

@Thickness 2.00 mm
 25

@Thickness 0.0787 in
 H-18 wheel; ASTM D-1044; molded plaque, cured 20 hr at 100°C.
Compression Set 25 %
25 %
22 hr at 23°C per ASTM D-395; 2.0 mm (0.080 in) molded plaque, cured 20 hr at 100°C.
45 %

@Temperature 70.0 °C
 45 %

@Temperature 158 °F
 22 hr @ 70°C; ASTM D-395; 0.080 in molded plaque after curing 20 hrs at 100°C.
Tensile Set 32 %
32 %
at 200% elongation per ASTM D-412 is on 0.030 in extruded sheet.
Thermal Properties Metric English Comments
Vicat Softening Point 100 °C

@Thickness 2.00 mm
 212 °F

@Thickness 0.0787 in
 molded plaque, cured 20 hr at 100°C.; ASTM D1525
Glass Transition Temp, Tg -40.0 °C
-40.0 °F
Pellet sample