Hexcel® HexPly® F155 Epoxy Resin, 181 Glass Fabric

Category Polymer , Thermoset , Epoxy , Epoxy/Glass SMC
Manufacturer Hexcel
Trade Name HexPly®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Hexcel® HexPly® F155 Epoxy Resin, 181 Glass Fabric.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by HexCel
Mechanical Properties Metric English Comments
Tensile Strength, Yield 4.206 MPa

@Temperature 93.0 °C
 610.0 psi

@Temperature 199 °F
 Flatwise TS
4.826 MPa

@Temperature 71.0 °C
 700.0 psi

@Temperature 160 °F
 Flatwise TS
5.378 MPa

@Temperature 24.0 °C
 780.0 psi

@Temperature 75.2 °F
 Flatwise TS
393 MPa

@Temperature 93.0 °C
 57000 psi

@Temperature 199 °F
427 MPa

@Temperature 71.0 °C
 61900 psi

@Temperature 160 °F
483 MPa

@Temperature 24.0 °C
 70100 psi

@Temperature 75.2 °F
Tensile Modulus 20.0 GPa

@Temperature 93.0 °C
 2900 ksi

@Temperature 199 °F
21.4 GPa

@Temperature 71.0 °C
 3100 ksi

@Temperature 160 °F
23.4 GPa

@Temperature 24.0 °C
 3390 ksi

@Temperature 75.2 °F
Compressive Yield Strength 331 MPa

@Temperature 93.0 °C
 48000 psi

@Temperature 199 °F
400 MPa

@Temperature 71.0 °C
 58000 psi

@Temperature 160 °F
517 MPa

@Temperature 24.0 °C
 75000 psi

@Temperature 75.2 °F
Compressive Modulus 22.1 GPa

@Temperature 93.0 °C
 3210 ksi

@Temperature 199 °F
23.4 GPa

@Temperature 71.0 °C
 3390 ksi

@Temperature 160 °F
25.5 GPa

@Temperature 24.0 °C
 3700 ksi

@Temperature 75.2 °F
Shear Strength 68.9 MPa
9990 psi
Compression interlaminar; RT
37.0 MPa

@Temperature 93.0 °C
 5370 psi

@Temperature 199 °F
 Compression interlaminar
48.0 MPa

@Temperature 71.0 °C
 6960 psi

@Temperature 160 °F
 Compression interlaminar