- Saint-Gobain Meldin® 7211 CM Compression Molded Graphite and PTFE Filled Polyimide
Saint-Gobain Meldin® 7211 CM Compression Molded Graphite and PTFE Filled Polyimide
| Category | Polymer , Thermoset , Polyimide, TS |
| Manufacturer | Saint-Gobain Perfomance Plastics |
| Trade Name | Meldin® |
| Port | Ningbo port,China |
| Trade Terms | EXW, FOB, CFR, CIF |
| Payment Terms | L/C, T/T, PayPal |
| Download PDF | Saint-Gobain Meldin® 7211 CM Compression Molded Graphite and PTFE Filled Polyimide.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Melidin® 7211 CM is a compression molded polyimide that contains 15% graphite and 10% PTFE fillers. This grade has the lowest coefficient of friction of the Meldin® 7000 series polyimides.Specification Qualifications:Satisfies Type II, Class 3P for ASTM D 6456-99: Standard Specification for Finished Parts Made from Polyimide ResinSatisfies Class 4, Form P for SAE AMS 3644G: Polyimide, Molded Rod, Bar and Tube, Plaque, and Formed PartsSatisfies Type II, Class 3P for MIL-R-46198: Resin, Polyimide, Hot Pressed or Pressed and SinteredInformation provided by Saint-Gobain Performance Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.53 g/cc | 0.0553 lb/in³ | ASTM D792 |
| Water Absorption | 0.23 % <br>@Time 86400 sec |
0.23 % <br>@Time 24.0 hour |
ASTM D570 |
| 0.46 % <br>@Time 173000 sec |
0.46 % <br>@Time 48.0 hour |
ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell E | 1.0 - 15 | 1.0 - 15 | ASTM D785 |
| Tensile Strength | 29.6 MPa <br>@Temperature 260 °C |
4300 psi <br>@Temperature 500 °F |
ASTM D638 |
| 37.9 MPa <br>@Temperature 170 °C |
5500 psi <br>@Temperature 338 °F |
ASTM D638 | |
| 41.4 MPa <br>@Temperature 130 °C |
6000 psi <br>@Temperature 266 °F |
ASTM D638 | |
| 51.7 MPa <br>@Temperature 23.0 °C |
7500 psi <br>@Temperature 73.4 °F |
ASTM D638 | |
| Elongation at Break | 2.8 % <br>@Temperature 260 °C |
2.8 % <br>@Temperature 500 °F |
ASTM D638 |
| 4.0 % <br>@Temperature 23.9 °C |
4.0 % <br>@Temperature 75.0 °F |
ASTM D638 | |
| Flexural Strength | 41.4 MPa <br>@Temperature 260 °C |
6000 psi <br>@Temperature 500 °F |
ASTM D790 |
| 81.4 MPa <br>@Temperature 23.9 °C |
11800 psi <br>@Temperature 75.0 °F |
ASTM D790 | |
| Flexural Modulus | 2.10 GPa <br>@Temperature 260 °C |
305 ksi <br>@Temperature 500 °F |
ASTM D790 |
| 3.40 GPa <br>@Temperature 23.9 °C |
493 ksi <br>@Temperature 75.0 °F |
ASTM D790 | |
| Compressive Yield Strength | 24.1 MPa <br>@Strain 1.00 % |
3500 psi <br>@Strain 1.00 % |
ASTM D695 |
| 103.1 MPa <br>@Strain 10.0 % |
14950 psi <br>@Strain 10.0 % |
ASTM D695 | |
| Compressive Modulus | 2.40 GPa | 348 ksi | ASTM D695 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 43.2 µm/m-°C <br>@Temperature 22.8 - 260 °C |
24.0 µin/in-°F <br>@Temperature 73.0 - 500 °F |
ASTM E831 |
| Thermal Conductivity | 0.749 W/m-K | 5.20 BTU-in/hr-ft²-°F | ASTM F433 |
Users viewing this material also viewed the following:
- MV Labs IN110 In(C2H3O2)3 Indium(III) acetate, anhydrous
- Polykemi AB SCANMID 6 B11^ F30 Nylon 6, Glass Fiber Reinforced
- S&E Specialty Polymers TufTech™ GA-1050 PVC Compound
- NOVA Chemicals Sclair® 10B Octene VLDPE Film Resin (discontinued **)
- Karina 18/219-RG-GE (CS) Gray Color Concentrate for PVC
- TIMET 6-4 Titanium Alloy (Ti-6Al-4V; ASTM Grade 5), >0.500-1.000 in, STD, Per Mil-T-9047G
- Clariant Renol PBT1100S Polybutylene Terephthalate, Silicone Lubricated
- 3M Scotch-Weld™ 3794 Hi Tack PSA Bulk only Adhesive
- Addiplast Addinyl C2 ZV15 Nylon 66/6, 15% Glass Filled
- E-Polymers TEKAFIN® PH50GM 30% Glass Fiber Reinforced Mineral Filled Low Warpage Compounded-PP
Copyright © lookpolymers.com All Rights Reserved