- SCG Chemicals EL-Leneâ„¢ H1000PBL High Density Polyethylene Pipe Resin
SCG Chemicals EL-Leneâ„¢ H1000PBL High Density Polyethylene Pipe Resin
| Category | Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Pipe Grade |
| Manufacturer | SCG Chemicals Co. |
| Trade Name | EL-Lene™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SCG Chemicals EL-Leneâ„¢ H1000PBL High Density Polyethylene Pipe Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Key Characteristics: Good processing, high thermal stability, good resistance to weathering, good balance of MRS and SCGRecommended Applications: Water pressure pipes and stripe lines for PE100 pipeCertification: Certified by EXOVA, LNEInformation provided by SCG Chemicals
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.951 g/cc | 0.951 g/cc | ISO 1183 |
| Environmental Stress Crack Resistance | >= 10000 hour | >= 10000 hour | F0; ASTM D1693 |
| Oxidative Induction Time (OIT) | >= 70 min @Temperature 200 °C |
>= 70 min @Temperature 392 °F |
ISO/TR10837 |
| Melt Flow | 0.28 g/10 min @Load 5.00 kg, Temperature 190 °C |
0.28 g/10 min @Load 11.0 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 66 | 66 | ASTM D2240 |
| Tensile Strength at Break | 36.0 MPa | 5220 psi | Crosshead speed 100 mm/min; ISO 527 |
| Tensile Strength, Yield | 23.0 MPa | 3340 psi | Crosshead speed 100 mm/min; ISO 527 |
| Elongation at Break | 850 % | 850 % | Crosshead speed 100 mm/min; ISO 527 |
| Flexural Modulus | 0.900 GPa | 131 ksi | ASTM D790 |
| Izod Impact, Notched | 1.96 J/cm @Temperature -20.0 °C |
3.67 ft-lb/in @Temperature -4.00 °F |
ASTM D256 |
| 2.65 J/cm @Temperature 0.000 °C |
4.96 ft-lb/in @Temperature 32.0 °F |
ASTM D256 | |
| 3.04 J/cm @Temperature 23.0 °C |
5.69 ft-lb/in @Temperature 73.4 °F |
ASTM D256 | |
| Hydrostatic Design Basis | 10.0 MPa | 1450 psi | ISO 9080 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Brittleness Temperature | <= -60.0 °C | <= -76.0 °F | ASTM D746 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Carbon Black/Pigment Dispersion (grade) | <3 | ISO 18553 |
| Color | Blue | RAL5005 |
| Resistance to Slow Crack Growth | >1000 hours | ISO 13479 |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 6 G 5 Polyamide 6, 5% Graphite
- MV Labs ZN600 ZnI2 Zinc iodide
- PolyOne reFlex™ 100 Plasticizer, Bio-derived
- Parker Chomerics CHO-FORM 5525, Part A Silicone
- PolyOne Edgetek® AS-20GF/000 HI UV NAT Acrylonitrile Butadiene Styrene (ABS), Glass Filled (discontinued **)&
- Covestro Baydur® 660 IBS Polyurethane Structural Foam RIM, Density 40 pcf, MDI-based 2-Component Liquid System
- Colorite Polymers 8002 General Purpose Vinyl Compound
- ChevronTexaco Pinnacle® 460
- Huntsman PE2049 Injection Molding Polyethylene (discontinued **)
Copyright © lookpolymers.com All Rights Reserved