SABIC Innovative Plastics Xenoy® X5500EX PBT+PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Xenoy® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Xenoy® X5500EX PBT+PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Non-FR, non-UV PC/PBT blend for film extrusion application
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.24 g/cc | 1.24 g/cc | ASTM D792 |
| Water Absorption at Saturation | 0.040 % | 0.040 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0060 - 0.0080 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 6.5 g/10 min @Load 5.00 kg, Temperature 250 °C |
6.5 g/10 min @Load 11.0 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 62.0 MPa | 8990 psi | Type I, 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 65.0 MPa | 9430 psi | Type I, 50 mm/min; ASTM D638 |
| Elongation at Break | 95 % | 95 % | Type I, 50 mm/min; ASTM D638 |
| Elongation at Yield | 5.5 % | 5.5 % | Type I, 50 mm/min; ASTM D638 |
| Tensile Modulus | 2.46 GPa | 357 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 95.0 MPa | 13800 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Yield Strength | 98.0 MPa | 14200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 2.28 GPa | 331 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 1.05 J/cm | 1.97 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 21.6 J/cm | 40.5 ft-lb/in | ASTM D4812 |
| Dart Drop, Total Energy | 70.0 J @Temperature 23.0 °C |
51.6 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 123 °C @Thickness 6.40 mm |
253 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 108 °C @Thickness 6.40 mm |
226 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Vicat Softening Point | 132 °C | 270 °F | Rate B/50; ASTM D1525 |
Users viewing this material also viewed the following:
- Polykemi AB POLYblend 45FS PC/ABS-blend, Flame Retardant
- Proto3000 Objet Digital Materials™ DM_9885/9785 Rubber-like Prototyping Polymer
- Kazanorgsintez Aluminum Hydroxychloride
- Lubriplate Super 345, SAE 5W-30 Long Mileage Motor Oil Motor Oil & Transmission Fluid
- Schott Glass 8660 Borosilicate Glass
- Epoxy Technology EPO-TEK® H20-LC Electrically Conductive, Silver Epoxy
- Chosun Refractories APN-1 Special brick
- Eurostar Starflam AFR450B PA66, 25% Glass Fiber Reinforced, Flame Retardant, Injection Molding
- BASF Triethylamine TEA
Copyright © lookpolymers.com All Rights Reserved