SABIC Innovative Plastics Xenoy® 6620 PBT+PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Xenoy® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Xenoy® 6620 PBT+PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Impact modified, highly chemical resistant polyester/polycarbonate alloy.This data was supplied by SABIC-IP for the Asia Pacific region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D 792 |
| Linear Mold Shrinkage, Flow | 0.014 - 0.020 cm/cm @Thickness 3.20 mm |
0.014 - 0.020 in/in @Thickness 0.126 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 43.0 MPa | 6240 psi | Type I, 50 mm/min; ASTM D 638 |
| Elongation at Break | 175 % | 175 % | Type I, 50 mm/min; ASTM D 638 |
| Flexural Yield Strength | 64.0 MPa | 9280 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 1.72 GPa | 249 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Izod Impact, Notched | 8.01 J/cm @Temperature 23.0 °C |
15.0 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C @Thickness 6.40 mm |
140 °F @Thickness 0.252 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- Lubriplate 68-N Naphthenic Refrigeration Compressor Oil
- Solvay Specialty Polymers Amodel® A-1933 HSL Polyphthalamide (PPA), 33% Glass Fiber
- Shandong Rike Chemical HELIâ„¢ HL-275 PVC Processing Aid Series (PA)
- DuPont Bynel® 4104 Anhydride-Modified LLDPE Adhesive Resin
- UBE UBEPOL BR153A Oil-Extended Synthetic Rubber (Raw Polymer)
- DuPont Teijin Films Melinex® 329 Polyester Film, 75 Gauge
- ExxonMobil Exxelor™ PE 1040 High Density Polyethylene Resin
- Sumitomo Bakelite North America Epiall® 1914A Short Glass Fiber Reinforced Epoxy
- EMS-Griltech Grilon® BA 140 White Nylon 66/CoPA Bi-Component Fiber
- Victrex® Vicote® 701 Polyetheretherketone (PEEK) Powder
Copyright © lookpolymers.com All Rights Reserved