SABIC Innovative Plastics Valox® V9290 PET (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Valox® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Valox® V9290 PET (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
45% GF PET, Glass, Mold Release, Heat Stabilized,
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.65 g/cc | 0.0596 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.0500 % | 0.0500 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.25 % | 0.25 % | ISO 62 |
| Melt Index of Compound | 7.0 g/10 min @Load 1.20 kg, Temperature 265 °C |
7.0 g/10 min @Load 2.65 lb, Temperature 509 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 160 MPa | 23200 psi | 5 mm/min; ISO 527 |
| Tensile Strength, Yield | 160 MPa | 23200 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 1.5 % | 1.5 % | 5 mm/min; ISO 527 |
| Elongation at Yield | 1.5 % | 1.5 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 15.0 GPa | 2180 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 225 MPa | 32600 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 13.0 GPa | 1890 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | 80*10*4; ISO 180/1A |
| 8.00 kJ/m² @Temperature -30.0 °C |
3.81 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 0.700 J/cm² | 3.33 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
11.1 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
44.4 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Vicat Softening Point | 235 °C | 455 °F | Rate B/50; ISO 306 |
| 240 °C | 464 °F | Rate B/120; ISO 306 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics LNP Faradex DS0036IP PC (Asia Pacific)
- Ipiranga Petrochem GM 7746 HDPE
- Taiwan Sheen Soon Sheenthane® A9660 Thermoplastic Polyurethane Elastomer
- Solvay Specialty Polymers Ixef® 1524 Polyarylamide (PARA), 50% Glass Fiber (Dry)
- SABIC Innovative Plastics Noryl FXN2090H PPE+HIPS
- A. Schulman POLYBLAK™ 3209 Superior Black Color Concentrate, 40% Carbon Black Based In Polypropylene
- Dow Corning Z-6076 SILANE
- Clariant Renol PA611D40 Nylon 612, Glass Fiber Reinforced, Molybdenum Disulfide Lubricated
- Loctite® Durabond® E-00CL Epoxy Adhesive
- Overview of materials for ABS/PVC Alloy
Copyright © lookpolymers.com All Rights Reserved