SABIC Innovative Plastics Ultem HTX1010F PEI (Asia Pacific)

Category Polymer , Thermoplastic , Polyetherimide (PEI)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name ULTEM
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Ultem HTX1010F PEI (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Higher impact, Polyetherimide (Tg 217C). ECO Conforming. US FDA Food Contact compliant.This data was supplied by SABIC-IP for the Asia Pacific region.
Physical Properties Metric English Comments
Specific Gravity 1.26 g/cc
1.26 g/cc
ASTM D 792
Melt Flow 15.5 g/10 min

@Load 6.60 kg,
Temperature 337 °C
 15.5 g/10 min

@Load 14.6 lb,
Temperature 639 °F
 ASTM D 1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 82.0 MPa
11900 psi
Type I, 5 mm/min; ASTM D 638
Tensile Strength, Yield 93.0 MPa
13500 psi
Type I, 5 mm/min; ASTM D 638
Elongation at Break 40 %
40 %
Type I, 5 mm/min; ASTM D 638
Tensile Modulus 3.10 GPa
450 ksi
5 mm/min; ASTM D 638
Flexural Yield Strength 137 MPa
19900 psi
2.6 mm/min, 100 mm span; ASTM D 790
Flexural Modulus 3.03 GPa
439 ksi
2.6 mm/min, 100 mm span; ASTM D 790
Izod Impact, Notched 1.60 J/cm

@Temperature 23.0 °C
 3.00 ft-lb/in

@Temperature 73.4 °F
 ASTM D 256
17.62 J/cm

@Thickness 3.20 mm
 33.01 ft-lb/in

@Thickness 0.126 in
 reverse notched; ASTM D 256
Izod Impact, Unnotched 20.82 J/cm

@Temperature 23.0 °C
 39.00 ft-lb/in

@Temperature 73.4 °F
 ASTM D 4812
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 196 °C

@Thickness 6.40 mm
 385 °F

@Thickness 0.252 in
 unannealed; ASTM D 648
Glass Transition Temp, Tg 217 °C
423 °F
Oxygen Index 39.7 %
39.7 %
LOI; ASTM D 2863