SABIC Innovative Plastics ULTEM AUT200 PEI (Europe-Africa-Middle East)

Category	Polymer , Thermoplastic , Polyetherimide (PEI)
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	ULTEM
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics ULTEM AUT200 PEI (Europe-Africa-Middle East).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Transparent high flow Polyetherimide (Tg 217C). Very low outgassing and plateout, for automotive lighting applications where highly metallized, reflective surfaces are required. Haze onset temperature of 204C (SABIC IP method)

Physical Properties	Metric	English	Comments
Density	1.27 g/cc	0.0459 lb/in³	ISO 1183
Moisture Absorption	0.700 %	0.700 %	23°C / 50% RH; ISO 62
Water Absorption at Saturation	1.25 %	1.25 %	ISO 62
Linear Mold Shrinkage, Flow	0.0050 - 0.0070 cm/cm @Thickness 3.20 mm	0.0050 - 0.0070 in/in @Thickness 0.126 in	SABIC Method
Linear Mold Shrinkage, Transverse	0.0050 - 0.0070 cm/cm @Thickness 3.20 mm	0.0050 - 0.0070 in/in @Thickness 0.126 in	SABIC Method
Melt Index of Compound	25 g/10 min @Load 5.00 kg, Temperature 360 °C	25 g/10 min @Load 11.0 lb, Temperature 680 °F	MVR [cm^3/10 min]; ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	85.0 MPa	12300 psi	5 mm/min; ISO 527
Tensile Strength, Yield	105 MPa	15200 psi	5 mm/min; ISO 527
Elongation at Break	60 %	60 %	5 mm/min; ISO 527
Elongation at Yield	6.0 %	6.0 %	5 mm/min; ISO 527
Tensile Modulus	3.20 GPa	464 ksi	1 mm/min; ISO 527
Flexural Yield Strength	160 MPa	23200 psi	2 mm/min; ISO 178
Flexural Modulus	3.30 GPa	479 ksi	2 mm/min; ISO 178
Izod Impact, Notched (ISO)	5.00 kJ/m²	2.38 ft-lb/in²	80104; ISO 180/1A
	5.00 kJ/m² @Temperature -30.0 °C	2.38 ft-lb/in² @Temperature -22.0 °F	80104; ISO 180/1A
Izod Impact, Unnotched (ISO)	NB	NB	80104; ISO 180/1U
	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F	80104; ISO 180/1U
Charpy Impact, Notched	0.300 J/cm²	1.43 ft-lb/in²	Edgew 80104 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy	33.0 J @Temperature 23.0 °C	24.3 ft-lb @Temperature 73.4 °F	ASTM D3763

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	50.0 µm/m-°C @Temperature 23.0 - 150 °C	27.8 µin/in-°F @Temperature 73.4 - 302 °F	ISO 11359-2
CTE, linear, Transverse to Flow	50.0 µm/m-°C @Temperature 23.0 - 150 °C	27.8 µin/in-°F @Temperature 73.4 - 302 °F	ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi)	200 °C	392 °F	Edgew 120104 sp=100mm; ISO 75/Be
Deflection Temperature at 1.8 MPa (264 psi)	190 °C	374 °F	Edgew 120104 sp=100mm; ISO 75/Ae
	193 °C	379 °F	Flatw 80104 sp=64mm; ISO 75/Af
Vicat Softening Point	211 °C	412 °F	Rate B/50; ISO 306
	212 °C	414 °F	Rate B/120; ISO 306
	215 °C	419 °F	Rate A/50; ISO 306
Glass Transition Temp, Tg	217 °C	423 °F
Flame Spread	0.000 - 5.00 mm/min @Thickness 2.00 mm	0.000 - 0.197 in/min @Thickness 0.0787 in	FMVSS 302

Optical Properties	Metric	English	Comments
Transmission, Visible	90 %	90 %	transparent; thickness not quantified

Descriptive Properties	Value	Comments
Metallized Haze Onset	204°C	SABIC Method