SABIC Innovative Plastics ULTEM ATX200R PEI+PCE (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) , Polyetherimide (PEI) + PCE |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | ULTEM |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics ULTEM ATX200R PEI+PCE (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High flow Polyetherimide blend with internal mold release. ECO Conforming.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.26 g/cc | 1.26 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 26.5 g/10 min @Load 6.60 kg, Temperature 337 °C |
26.5 g/10 min @Load 14.6 lb, Temperature 639 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 96.0 MPa | 13900 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 70 % | 70 % | Type I, 5 mm/min; ASTM D638 |
| Flexural Yield Strength | 144 MPa | 20900 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Flexural Modulus | 3.17 GPa | 460 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Izod Impact, Notched | 0.530 J/cm | 0.993 ft-lb/in | ASTM D256 |
| 21.36 J/cm @Thickness 3.20 mm |
40.02 ft-lb/in @Thickness 0.126 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C @Thickness 6.40 mm |
374 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Nylene® 601 Nylon 6, 50% RH, Extrusion Grade
- DSM Arnitel® EB500 50 Shore D, Blow Molding Grade Copolyester Elastomer (North America) (discontinued **)
- Chevron Phillips mPact™ D352 m-LLDPE Linear Low Density Polyethylene (discontinued **)
- DuPont Teijin Films Melinex® 329S Polyester Film, 92 Gauge
- Arkema Group Rilsamid® PA 12 AESNO MED Nylon 12
- Bhansali Engineering Abstron AN-450 Flame Retardant ABS Grade
- Dymax Magnet Bonder™ 2000 Adhesive
- LATI LAESTRA G/40-V0CT1 40% Glass Fiber Reinforced, Elastomer Modified, Flame Retardant Syndiotactic Polystyrene (SPS)
- Polyram Polytron P30N07 Polypropylene, 30% Long Glass Fiber, UV Stabilized
Copyright © lookpolymers.com All Rights Reserved