SABIC Innovative Plastics ULTEM 2110R PEI (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | ULTEM |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics ULTEM 2110R PEI (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
10% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, UL94 V0 and 5VA listing.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.34 g/cc | 1.34 g/cc | ASTM D792 |
| Melt Flow | 11.5 g/10 min @Load 6.60 kg, Temperature 337 °C |
11.5 g/10 min @Load 14.6 lb, Temperature 639 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 115 MPa | 16700 psi | Type I, 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 114 MPa | 16500 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 6.0 % | 6.0 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 4.61 GPa | 669 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 199 MPa | 28900 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Flexural Modulus | 5.24 GPa | 760 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Izod Impact, Notched | 0.530 J/cm | 0.993 ft-lb/in | ASTM D256 |
| 4.00 J/cm @Thickness 3.20 mm |
7.49 ft-lb/in @Thickness 0.126 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 207 °C @Thickness 6.40 mm |
405 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Glass Transition Temp, Tg | 217 °C | 423 °F | |
| UL RTI, Electrical | 170 °C | 338 °F | UL 746B |
| UL RTI, Mechanical with Impact | 170 °C | 338 °F | UL 746B |
| UL RTI, Mechanical without Impact | 170 °C | 338 °F | UL 746B |
| Flammability, UL94 | V-0 @Thickness 0.400 mm |
V-0 @Thickness 0.0157 in |
UL 94 |
| 5VA @Thickness 1.90 mm |
5VA @Thickness 0.0748 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Arc Resistance | 60 - 120 sec | 60 - 120 sec | Tungsten; ASTM D495 |
| Comparative Tracking Index | 100 - 175 V | 100 - 175 V | UL 746A |
| Hot Wire Ignition, HWI | 60 - 120 sec | 60 - 120 sec | UL 746A |
| High Amp Arc Ignition, HAI | 0.00 - 15 arcs | 0.00 - 15 arcs | UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | 25.4 - 80.0 mm/min | 1.00 - 3.15 in/min | UL 746A |
Users viewing this material also viewed the following:
- Ravago Manufacturing Americas Hylex® P1310FRMA Polycarbonate
- Ineos N12Z-00 Polypropylene Impact Copolymer
- Lanxess Durethan® DP BKV 35 XF 901510 Nylon 6, 35% Glass Fiber
- Lubrizol Estane® 2103-90AEFH Thermoplastic Polyurethane Elastomer
- DSM Akulon® K223-HM6 (BLACK) Nylon 6-30% Mineral Reinforced (European and Asian Grade) (Dry)
- ExxonMobil SpectraSyn™ 40 Polyalphaolefin (PAO) Fluid
- Assab Steels 707 Machinery Steel
- American Computer Optics Medium-High Transmission Filter 3 mm
- 3M Dyneon™ Aflas® FA-100H PTFE Fluoroelastomer (discontinued **)
Copyright © lookpolymers.com All Rights Reserved