SABIC Innovative Plastics Noryl PX4058 PPE+PS

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Noryl
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Noryl PX4058 PPE+PS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PPO, polyolefin blend. Improved chemical resistance. 253F (125C) HDT.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Specific Gravity 1.06 g/cc
1.06 g/cc
ASTM D 792
Water Absorption 0.070 %

@Time 86400 sec
0.070 %

@Time 24.0 hour
ASTM D 570
Mechanical Properties Metric English Comments
Hardness, Rockwell R 96
96
ASTM D 785
Tensile Strength, Yield 44.0 MPa
6380 psi
Type I, 50 mm/min; ASTM D 638
Elongation at Break 114 %
114 %
Type I, 50 mm/min; ASTM D 638
Flexural Yield Strength 64.0 MPa
9280 psi
2.6 mm/min, 100 mm span; ASTM D 790
Flexural Modulus 1.79 GPa
260 ksi
2.6 mm/min, 100 mm span; ASTM D 790
Izod Impact, Notched 1.49 J/cm

@Temperature -40.0 °C
2.79 ft-lb/in

@Temperature -40.0 °F
ASTM D 256
4.80 J/cm

@Temperature 23.0 °C
8.99 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Izod Impact, Unnotched 2.67 J/cm

@Temperature -30.0 °C
5.00 ft-lb/in

@Temperature -22.0 °F
ASTM D 4812
19.81 J/cm

@Temperature 23.0 °C
37.11 ft-lb/in

@Temperature 73.4 °F
ASTM D 4812
Impact Test 2.00 J

@Temperature 23.0 °C
1.48 ft-lb

@Temperature 73.4 °F
Instrumented Impact Energy @ peak; ASTM D 3763
2.00 J

@Temperature -30.0 °C
1.48 ft-lb

@Temperature -22.0 °F
Instrumented Impact Energy @ peak; ASTM D 3763
Taber Abrasion, mg/1000 Cycles 8.0

@Load 1.00 kg
8.0

@Load 2.20 lb
CS-17; ASTM D 1044
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 140 °C

@Thickness 6.40 mm
284 °F

@Thickness 0.252 in
unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 122 °C

@Thickness 6.40 mm
252 °F

@Thickness 0.252 in
unannealed; ASTM D 648